Polymer Property : Modulus of Elasticity = 29300 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, weld metal as welded
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man..
Modulus of Elasticity 202 GPa

@Temperature 300 °C
29300 ksi

@Temperature 572 °F
Dynamic
Haynes 282® Nickel Alloy Autogenously Welded Sheet
Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Modulus of Elasticity 202 GPa

@Temperature 300 °C
29300 ksi

@Temperature 572 °F
Dynamic
Haynes 282® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate
Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Modulus of Elasticity 202 GPa

@Temperature 300 °C
29300 ksi

@Temperature 572 °F
Dynamic
Haynes 282® Nickel Alloy Sheet, Plate and Bar, Solution Annealed
Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Modulus of Elasticity 202 GPa

@Temperature 300 °C
29300 ksi

@Temperature 572 °F
Dynamic
Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened
Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Modulus of Elasticity 202 GPa

@Temperature 300 °C
29300 ksi

@Temperature 572 °F
Dynamic
Haynes 282® Nickel Alloy Sheet, Solution Annealed and Cold Worked
Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Modulus of Elasticity 202 GPa

@Temperature 300 °C
29300 ksi

@Temperature 572 °F
Dynamic
Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform
Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Modulus of Elasticity 202 GPa

@Temperature 300 °C
29300 ksi

@Temperature 572 °F
Dynamic
Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate
Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la..
Modulus of Elasticity 202 GPa

@Thickness 12.7 mm,
Temperature 316 °C
29300 ksi

@Thickness 0.500 in,
Temperature 600 °F
(Heat treated at 1066°C (1950°F), rapid quenched, plate)
HP Alloys Alloy B-2, Solution Treated, 10% Cold Worked
Solution Treated, 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.
Modulus of Elasticity 202 GPa

@Thickness 12.7 mm,
Temperature 316 °C
29300 ksi

@Thickness 0.500 in,
Temperature 600 °F
(Heat treated at 1066°C (1950°F), rapid quenched, plate)
HP Alloys Alloy B-2, Solution Treated, 20% Cold Worked
Solution Treated, 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.
Modulus of Elasticity 202 GPa

@Thickness 12.7 mm,
Temperature 316 °C
29300 ksi

@Thickness 0.500 in,
Temperature 600 °F
(Heat treated at 1066°C (1950°F), rapid quenched, plate)
HP Alloys Alloy B-2, Solution Treated, 30% Cold Worked
Solution Treated, 30% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.
Modulus of Elasticity 202 GPa

@Thickness 12.7 mm,
Temperature 316 °C
29300 ksi

@Thickness 0.500 in,
Temperature 600 °F
(Heat treated at 1066°C (1950°F), rapid quenched, plate)
HP Alloys Alloy B-2, Solution Treated, 40% Cold Worked
Solution Treated, 40% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.
Modulus of Elasticity 202 GPa

@Temperature 400 °C
29300 ksi

@Temperature 752 °F
Typical annealed sample; short time elevated temp.
American Utility Metals Cromgard® Stainless Steel
Cromgard is a low cost stainless steel, which is able to provide benefits of good weldability and formability, making it capable of fabrication by conventional techniques. It provides the benefits o..
Modulus of Elasticity 202 GPa

@Temperature 300 °C
29300 ksi

@Temperature 572 °F
Dynamic
Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened
Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Modulus of Elasticity 202 GPa

@Thickness 12.7 mm,
Temperature 316 °C
29300 ksi

@Thickness 0.500 in,
Temperature 600 °F
(Heat treated at 1066°C (1950°F), rapid quenched, plate)
HP Alloys Alloy B-2, Solution Treated, 50% Cold Worked
Solution Treated, 50% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.
Modulus of Elasticity 202 GPa

@Temperature 300 °C
29300 ksi

@Temperature 572 °F
Dynamic
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened
Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b..
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..
Modulus of Elasticity 202 GPa

@Temperature 221 °C
29300 ksi

@Temperature 430 °F
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..