- Polymer Property : Modulus of Elasticity = 24100 ksi
Polymer Property : Modulus of Elasticity = 24100 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 700 °C |
24100 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® X alloy, sheet Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095°C, and good carburization resistance. Applications includ.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 816 °C |
24100 ksi @Temperature 1500 °F |
|
| Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 816 °C |
24100 ksi @Temperature 1500 °F |
|
| Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 800 °C |
24100 ksi @Temperature 1470 °F |
Dynamic |
| Haynes 282® Nickel Alloy Autogenously Welded Sheet Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 800 °C |
24100 ksi @Temperature 1470 °F |
Dynamic |
| Haynes 282® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 800 °C |
24100 ksi @Temperature 1470 °F |
Dynamic |
| Haynes 282® Nickel Alloy Sheet, Plate and Bar, Solution Annealed Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 800 °C |
24100 ksi @Temperature 1470 °F |
Dynamic |
| Haynes 282® Nickel Alloy Sheet, Solution Annealed and Age-hardened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 800 °C |
24100 ksi @Temperature 1470 °F |
Dynamic |
| Haynes 282® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 800 °C |
24100 ksi @Temperature 1470 °F |
Dynamic |
| Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Modulus of Elasticity | 166 GPa @Temperature 760 °C |
24100 ksi @Temperature 1400 °F |
Heat treated at 1066°C, air cooled |
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||