Polymer Property : Modulus of Elasticity = 182 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, gas tungsten arc welded
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, weld metal, aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, weld metal, aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application..
Modulus of Elasticity 182 GPa

@Temperature 593 °C
26400 ksi

@Temperature 1100 °F
Haynes R-41 alloy,
Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity 182 GPa

@Temperature 593 °C
26400 ksi

@Temperature 1100 °F
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F)
Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity 182 GPa

@Temperature 593 °C
26400 ksi

@Temperature 1100 °F
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121°C, air cooled, aged 16 hours at 899°C
Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..
Modulus of Elasticity 182 GPa

@Temperature 593 °C
26400 ksi

@Temperature 1100 °F
Haynes R-41 alloy,
Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include ..
Modulus of Elasticity 182 GPa

@Temperature 538 °C
26400 ksi

@Temperature 1000 °F
Heat treated at 1066°C, air cooled
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications ..