- Polymer Property : Modulus of Elasticity = 171 GPa
Polymer Property : Modulus of Elasticity = 171 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 760 °C |
24800 ksi @Temperature 1400 °F |
|
| Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 760 °C |
24800 ksi @Temperature 1400 °F |
|
| Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 760 °C |
24800 ksi @Temperature 1400 °F |
|
| Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 760 °C |
24800 ksi @Temperature 1400 °F |
|
| Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121°C, air cooled, aged 16 hours at 899°C Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 600 °C |
24800 ksi @Temperature 1110 °F |
Dynamic |
| Haynes 625SQ® Nickel Alloy Sheet Haynes 625SQ alloy is a solid-solution strengthened superalloy. It is a modification of Haynes 625 alloy designed to enhance resistance to fatigue at temperatures up to approximately 1200°F (649Â.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 538 °C |
24800 ksi @Temperature 1000 °F |
|
| Haynes Hastelloy® C-2000® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 538 °C |
24800 ksi @Temperature 1000 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 538 °C |
24800 ksi @Temperature 1000 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 538 °C |
24800 ksi @Temperature 1000 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 538 °C |
24800 ksi @Temperature 1000 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 538 °C |
24800 ksi @Temperature 1000 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 538 °C |
24800 ksi @Temperature 1000 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, rapid air cooled Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 760 °C |
24800 ksi @Temperature 1400 °F |
|
| Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include .. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 538 °C |
24800 ksi @Temperature 1000 °F |
|
| Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Modulus of Elasticity | 171 GPa @Temperature 700 °C |
24800 ksi @Temperature 1290 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||