Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP842 Paper Base Laminate
(discontinued **) Description: Paper reinforced phenolic grade with controlled conductivity. Mechanical strength similar to NP611. NP842 is semi-conductive on the surfaces and through the laminate.Thickness Tested: 0.. |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP313 Cotton Fabric Description: Canvas phenolic laminate with molybdenum disulfide lubricant. Mechanical properties slightly lower than NP310.Thickness Tested: 0.062", 0.125" & 0.500" |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP315 Cotton Fabric Description: Canvas phenolic laminate with graphite added as a solid lubricant. This material has improved wear properties under certain conditions. Material is conductive to electricity and should .. |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP319 Cotton Fabric Base Laminate Description: Bleached canvas combined with phenolic resin and graphite lubricant. Better moisture resistance and machining characteristics than NP315. |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP347 Cotton Fabric Description: Bleached canvas with high temperature phenolic resin with molybdenum disulfide lubricant. Low moisture absorption. Capable of 150°C continuous operation.Thickness Tested: 0.062", 0.1.. |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP615 Paper Base Laminate Description: Room temperature punching and shearing grade up to .125" thick. More flexible and lower mechanical properties than NP611. NP615 is produced with high resin content melamine impregnated .. |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP680 Paper Base Laminate Description: Hot punching grade with electrical properties between NP611 to NP631.Thickness Tested: 0.062", 0.125" & 0.500" |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP691 Paper Base Laminate Description: Flame resistant, room temperature punching grade. NP691 is very similar to NP612 in electrical properties and mechanical strength, with improved moisture resistance.Thickness Tested: 0... |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP310U Cotton Fabric Description: Utility grade canvas phenolic with properties similar to NP310E.Not certifiable to NEMA due to low crosswise flexural strength. Previously designated NP310C.Thickness Tested: 0.062", 0... |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP612 Paper Base Laminate Description: Room temperature punching and shearing grade up to .125" thick. More flexible and lower mechanical properties than NP611. Intended for applications where electrical and moisture require.. |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP625 Paper Base Laminate Description: Paper phenolic grade with better moisture resistance than NP612. Requires less heat to punch and shear than NP611. |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
CW; ASTM D229 |
Industrial Laminates/Norplex NP664 Paper Base Laminate Description: Low cost room temperature punching grade with mechanical and electrical properties similar to NP612. This version is made with pigment cover plies on the surface.Thickness Tested: 0.062.. |
|||
Modulus of Elasticity | 6.89 GPa @Thickness 1.57 mm |
1000 ksi @Thickness 0.0620 in |
LW; ASTM D229 |
Industrial Laminates/Norplex NP321 Cotton Fabric
(discontinued **) Description: NP321 consists of a fine weave cotton fabric (linen) impregnated with a phenolic resin binder. Applications include vanes for air and liquid pumps, and compressors. NP321 remains very f.. |