Polymer Property : 300% Modulus = 0.0108 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
300% Modulus	0.0108 GPa @Temperature 145 Â°C, Time 2100 sec	1.56 ksi @Temperature 293 Â°F, Time 0.583 hour	cured; ASTM D412
LG Chemical BR 1208 Polybutadiene Polymer Description: BR1208 is high cis- 1,4 polybutadiene polymer produced by a solution polymerization process employing a stereospecific catalyst to control microstructure, molecular weight and molecular..
300% Modulus	0.0108 GPa @Temperature 145 Â°C, Time 2100 sec	1.56 ksi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1721 High Acrylonitrile Polymer Description: SBR 1721 is an oil extended cold polymerization SBR with 37.5 parts of highly aromatic oil and styrene-butadiene copolymer of 40% bound styrene. Raw materials for this product are car..
300% Modulus	0.0108 GPa @Temperature 145 Â°C, Time 2100 sec	1.56 ksi @Temperature 293 Â°F, Time 0.583 hour	ASTM D412
LG Chemical SBR 1737 High Acrylonitrile Polymer Description: SBR 1737 is an oil extended cold polymerization SBR with 37.5 parts of Low PCA (PolyCyclic Aromatic) oil and styrene-butadiene copolymer of 37% bound styrene. Raw materials for this pr..
300% Modulus	0.0108 GPa	1.57 ksi
Taiwan PU Corporation TPU-E90 General Grade, Extrusion Molding Polyester Base TPU Thermoplastic Polyurethane (TPU), General Grade, Polyester Base, Extrusion MoldingInformation provided by Taiwan PU Corporation.
300% Modulus	0.0108 GPa	1.57 ksi
Taiwan PU Corporation TPU-EH90 High Hydrolysis Resistance, Extrusion Molding Polyether Base TPU Thermoplastic Polyurethane (TPU), High Hydrolysis Resistance, Polyether Base, Extrusion MoldingInformation provided by Taiwan PU Corporation.
300% Modulus	0.0108 GPa	1.57 ksi
Taiwan PU Corporation TPUI-E85 General Grade, Injection Molding Polyester Base TPU Thermoplastic Polyurethane (TPU), General Grade, Polyester Base, Injection MoldingInformation provided by Taiwan PU Corporation.
300% Modulus	0.0108 GPa	1.57 ksi
Taiwan PU Corporation TPUI-G85 High Wear Resistance, Injection Molding Polycaprolactone Base TPU Thermoplastic Polyurethane (TPU), High Wear Resistance, Polycaprolactone Base, Injection MoldingInformation provided by Taiwan PU Corporation.
300% Modulus	0.0108 GPa	1.57 ksi
Taiwan PU Corporation TPUI-H85 High Hydrolysis Resistance, Injection Molding Polyether Base TPU Thermoplastic Polyurethane (TPU), High Hydrolysis Resistance, Polyether Base, Injection MoldingInformation provided by Taiwan PU Corporation.