Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Adhesive Bond Strength | 26.9 MPa | 3900 psi | Lap shear, alum to alum, 1 hr @ 65°C |
Tra-Con Tra-Bond 516H02 Fiber Optic Adhesive TRA-BOND 516H02 is a low viscosity, room temperature or low temperature curing fiber optic adhesive with good stress relief, high adhesion, and low shrinkage upon cure. TRA-BOND 516H02 contains very.. |
|||
Adhesive Bond Strength | 26.9 MPa | 3900 psi | Lap shear, alum to alum, 1 hr @ 65°C |
Tra-Con Tra-Bond F113SC High Tg Fiber Optic Epoxy Adhesive TRA-BOND F113SC is a room temperature curing, high Tg and low viscosity adhesive formulated for terminating ALL TYPES of fiber optic connectors. It has also been used for bonding LED displays, lense.. |
|||
Adhesive Bond Strength | 26.9 MPa | 3900 psi | Lap shear, alum to alum, 1 hr @ 150°C |
Tra-Con Tra-Bond 226U01 High Temperature Controlled Flow Adhesive TRA-BOND 226U01 is a one-part, controlled flow adhesive with high temperature resistance.Information provided by Tra-Con Inc. |
|||
Adhesive Bond Strength | 26.9 MPa | 3900 psi | Grit blasted steel |
Loctite® PRISM® 4212 Instant Adhesive Gel Cyanoacrylate Bonding AdhesivesLoctite® technology has made the productivity promises of cyanoacrylate adhesives a reality with the industry's widest selection of high-performance, application-.. |
|||
Adhesive Bond Strength | 26.9 MPa @Temperature 25.0 °C |
3900 psi @Temperature 77.0 °F |
Aluminum-Aluminum tensile shear |
Armstrong A-12 Epoxy Adhesive, at 2:3 Mix Ratio Our most popular general-purpose, high viscosity adhesive for industry. Combines low toxicity with excellent physical properties, and offers a non-critical mixing ratio of 1:1 by weight. This rati.. |
|||
Adhesive Bond Strength | 26.9 MPa | 3900 psi | Steel-Steel; after optimum cure |
Armstrong A-34 Epoxy Adhesive This white paste material is a fast-curing adhesive with a working life of 20-25 minutes in a 100-gram mass. Mixing ratio is a convenient 1:1. A-34 has excellent wetting properties and is suggeste.. |
|||
Adhesive Bond Strength | 26.9 MPa @Temperature 25.0 °C |
3900 psi @Temperature 77.0 °F |
Aluminum-Aluminum tensile shear |
Armstrong A-661 Epoxy Adhesive A truly unique, two-component, room temperature curing thixotropic epoxy adhesive system, which exhibits good bond strength at service temperatures up to 400°F. Ideal for applications where resist.. |
|||
Adhesive Bond Strength | 26.9 MPa | 3900 psi | Steel/Steel; Varies with substrates |
Loctite® 648 High Strength/Rapid Cure Retaining Compound RetainersLoctite Corporation, the pioneer of anaerobic adhesives, has applied this technology to create retaining compounds that increase the shear strength of cylindrical, non-threaded assemblies. .. |