Polymer Property : Adhesive Bond Strength = 250 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Adhesive Bond Strength 1.72 MPa

@Temperature 82.2 °C
250 psi

@Temperature 180 °F
Aluminum-Aluminum tensile shear
Armstrong C-7/W Epoxy Adhesive, 2:3 Mix Ratio
A clear, unfilled, medium viscosity adhesive recommended for use with any Armstrong Activator. Physical property data included covers C-7 used with Activators W and H-20. All other Activators may ..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP AEP EPI Engineered Polymers
EP AEP is a new generation of Internetwork Polymers of polyurea and Epoxy, “Powered by Reactamine® Technology”. EP AEP was developed for a colorfast floor for both residential and industrial appl..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP EF EPI Engineered Polymers Extra Flex Polyurea
EP EF, Extra Flex Polyurea, “Powered by Reactamine® Technology, is a two component 100% solid Polyurea, with superior performance in industrial applications. EP EF displays extremely fast cure tim..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP LCP EPI Engineered Polymers Aromatic Polyurea
EP LCP Aromatic Polyurea, “Powered by Reactamine® Technology” is a two component 100% solid Polyurea (silicone optional) with superior performance in industrial applications. EP LCP displays extr..
Adhesive Bond Strength 1.72 MPa
250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP QSZ EPI Engineered Polymers Quick Set Epoxy with Zinc
EP QSZ Quick Set Epoxy with Zinc, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC’s (Volatile Organic Compound), self-leveling modified epoxy. This versatile new gene..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP 45 EPI Engineered Polymers Aliphatic Polyurea
EP RAP 45 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC is, aliphatic polyurea (silicone optional) coating, that was developed for UV stable (col..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP EPI Engineered Polymers Aliphatic Silicone Polyurea
EP RAP Aliphatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Aliphatic Polyurea (silicone optional) that has excellent UV stability (colorfast) with supe..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP-1567 EPI Engineered Polymers Aliphatic Polyurea
RAP-1567 HX is a two component 100% solids, no VOC’s, aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This new generat..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP-1567 HX EPI Engineered Polymers Aliphatic Polyurea
RAP-1567 is a two component 100% solids, no VOC’s, aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This new generation..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea
RAP-1567 SP is a two component 100% solids, no VOC’s, silicone aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This ne..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea
RAP-1567 SP-HX is a two component 100% solids, no VOC’s, silicone aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RASP EPI Engineered Polymers Aliphatic Silicone Polymer
EP RASP Aliphatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea that has excellent UV stability (colorfast) with superior performance in industria..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RPSP EPI Engineered Polymers Aliphatic Silicone Polymer
EP RPSP Aromatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea with superior performance in industrial applications. EP RPSP displays extremely fa..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RSP-AL EPI Engineered Polymers Aromatic Silicone Polyurea
EP RSP-AL, Aromatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea. This increases UV resistance without sacrificing physical properties. EP RSP-AL..
Adhesive Bond Strength 1.72 MPa
250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP WQS EPI Engineered Polymers Water Base Quick Set Epoxy
EP WQS Water Base Quick Set, “Powered by Reactamine® Technology”, is a two component 60% solids, no VOC, self-leveling modified epoxy. This versatile new generation epoxy displays low blush, fast..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC SMP™ EP EF SP EPI Engineered Polymers Extra Flex with Silicone
EP EF SP, “Powered by Reactamine® Technology”, is a two component 100% solid Silicone Polyurea with superior performance in industrial applications. EP EF SP displays extremely fast cure times wi..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP 60 EPI Engineered Polymers Aliphatic Polyurea
EP RAP 60 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, coating (silicone optional) developed for UV stable (colorfast) polyurea flooring applic..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RP EPI Engineered Polymers Aromatic Polyurea
EP RP, Aromatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea with superior performance in industrial applications. EP RP displays extremely fast cure time..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RSP EPI Engineered Polymers Silicone Polyurea
EP RSP Silicone Polyurea, “Powered by Reactamine®Technology”, is a two component 100% solid Polyurea with superior performance in industrial applications. EP RSP displays extremely fast cure time..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC SMP™ EP 1009 EPI Engineered Polymers Silicone Modified Polymer
EP 1009, “Powered by Reactamine®Technology”, is a two component 100% solid Silicone Modified Polyurea with superior performance in industrial applications. EP 1009 displays extremely fast cure ti..
Adhesive Bond Strength 1.72 MPa
250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP QS EPI Engineered Polymers Quick Set Epoxy
EP QS Quick Set Epoxy, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, self-leveling modified epoxy. This versatile new generation epoxy displays low blush, fast cure..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP 45 14 EPI Engineered Polymers Aliphatic Polyurea
EP RAP 45 14 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC’s, aliphatic polyurea coating that was developed for UV stable (colorfast) polyurea f..
Adhesive Bond Strength >= 1.72 MPa
>= 250 psi
Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC ReactAmine® EP 350 EPI Engineered Polymers Polyurea
ReactAmine® EP-350 is a two component 100% solid Polyurea with superior performance in industrial applications. EP-350 displays extremely fast cure times with excellent adhesions to different subst..