Polymer Property : Adhesive Bond Strength = 1.72 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Adhesive Bond Strength	1.72 MPa	249 psi	Acrylic, Substrate Failure, Shear; ASTM D1002
Permabond 930 Cyanoacrylate PERMABOND 930 is a low odor, nonfogging, nonfrosting cyanoacrylate. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesives on hot and humid days, is eliminated. The ..
Adhesive Bond Strength	1.72 MPa	249 psi	Acrylic Substrate Failure, Shear; ASTM D1002
Permabond 931 Cyanoacrylate PERMABOND 931 is a low odor, nonfogging, nonfrosting cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesiv..
Adhesive Bond Strength	1.72 MPa	249 psi	Acrylic Substrate Failure, Shear; ASTM D1002
Permabond 932 Cyanoacrylate PERMABOND 932 is a low odor, nonfogging, nonfrosting cyanoacrylate. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesiv..
Adhesive Bond Strength	1.72 MPa	249 psi	Acrylic, Substrate Failure, Shear; ASTM D1002
Permabond 935 Cyanoacrylate The PERMABOND 930 series is a family of low odor, non-fogging, non-frosting cyanoacrylates. The reduced odor improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyano..
Adhesive Bond Strength	1.72 MPa @Temperature 82.2 °C	250 psi @Temperature 180 °F	Aluminum-Aluminum tensile shear
Armstrong C-7/W Epoxy Adhesive, 2:3 Mix Ratio A clear, unfilled, medium viscosity adhesive recommended for use with any Armstrong Activator. Physical property data included covers C-7 used with Activators W and H-20. All other Activators may ..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP AEP EPI Engineered Polymers EP AEP is a new generation of Internetwork Polymers of polyurea and Epoxy, “Powered by Reactamine® Technology”. EP AEP was developed for a colorfast floor for both residential and industrial appl..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP EF EPI Engineered Polymers Extra Flex Polyurea EP EF, Extra Flex Polyurea, “Powered by Reactamine® Technology, is a two component 100% solid Polyurea, with superior performance in industrial applications. EP EF displays extremely fast cure tim..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP LCP EPI Engineered Polymers Aromatic Polyurea EP LCP Aromatic Polyurea, “Powered by Reactamine® Technology” is a two component 100% solid Polyurea (silicone optional) with superior performance in industrial applications. EP LCP displays extr..
Adhesive Bond Strength	1.72 MPa	250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP QSZ EPI Engineered Polymers Quick Set Epoxy with Zinc EP QSZ Quick Set Epoxy with Zinc, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC’s (Volatile Organic Compound), self-leveling modified epoxy. This versatile new gene..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP 45 EPI Engineered Polymers Aliphatic Polyurea EP RAP 45 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC is, aliphatic polyurea (silicone optional) coating, that was developed for UV stable (col..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP EPI Engineered Polymers Aliphatic Silicone Polyurea EP RAP Aliphatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Aliphatic Polyurea (silicone optional) that has excellent UV stability (colorfast) with supe..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP-1567 EPI Engineered Polymers Aliphatic Polyurea RAP-1567 HX is a two component 100% solids, no VOC’s, aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This new generat..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP-1567 HX EPI Engineered Polymers Aliphatic Polyurea RAP-1567 is a two component 100% solids, no VOC’s, aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This new generation..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea RAP-1567 SP is a two component 100% solids, no VOC’s, silicone aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This ne..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP-1567 SP-HX EPI Engineered Polymers Silicone Aliphatic Polyurea RAP-1567 SP-HX is a two component 100% solids, no VOC’s, silicone aliphatic polyureas “Powered by ReactAmine® Technology” that was developed for UV stable (colorfast) polyurea applications. This..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RASP EPI Engineered Polymers Aliphatic Silicone Polymer EP RASP Aliphatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea that has excellent UV stability (colorfast) with superior performance in industria..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RPSP EPI Engineered Polymers Aliphatic Silicone Polymer EP RPSP Aromatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea with superior performance in industrial applications. EP RPSP displays extremely fa..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RSP-AL EPI Engineered Polymers Aromatic Silicone Polyurea EP RSP-AL, Aromatic Silicone Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea. This increases UV resistance without sacrificing physical properties. EP RSP-AL..
Adhesive Bond Strength	1.72 MPa	250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP WQS EPI Engineered Polymers Water Base Quick Set Epoxy EP WQS Water Base Quick Set, “Powered by Reactamine® Technology”, is a two component 60% solids, no VOC, self-leveling modified epoxy. This versatile new generation epoxy displays low blush, fast..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC SMP™ EP EF SP EPI Engineered Polymers Extra Flex with Silicone EP EF SP, “Powered by Reactamine® Technology”, is a two component 100% solid Silicone Polyurea with superior performance in industrial applications. EP EF SP displays extremely fast cure times wi..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP 60 EPI Engineered Polymers Aliphatic Polyurea EP RAP 60 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, coating (silicone optional) developed for UV stable (colorfast) polyurea flooring applic..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RP EPI Engineered Polymers Aromatic Polyurea EP RP, Aromatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solid Polyurea with superior performance in industrial applications. EP RP displays extremely fast cure time..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RSP EPI Engineered Polymers Silicone Polyurea EP RSP Silicone Polyurea, “Powered by Reactamine®Technology”, is a two component 100% solid Polyurea with superior performance in industrial applications. EP RSP displays extremely fast cure time..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC SMP™ EP 1009 EPI Engineered Polymers Silicone Modified Polymer EP 1009, “Powered by Reactamine®Technology”, is a two component 100% solid Silicone Modified Polyurea with superior performance in industrial applications. EP 1009 displays extremely fast cure ti..
Adhesive Bond Strength	1.72 MPa	250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP QS EPI Engineered Polymers Quick Set Epoxy EP QS Quick Set Epoxy, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC, self-leveling modified epoxy. This versatile new generation epoxy displays low blush, fast cure..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC EP RAP 45 14 EPI Engineered Polymers Aliphatic Polyurea EP RAP 45 14 Aliphatic Polyurea, “Powered by Reactamine® Technology”, is a two component 100% solids, no VOC’s, aliphatic polyurea coating that was developed for UV stable (colorfast) polyurea f..
Adhesive Bond Strength	>= 1.72 MPa	>= 250 psi	Wood (no primer), Delamination; ASTM D4541 Elcometer
ACC ReactAmine® EP 350 EPI Engineered Polymers Polyurea ReactAmine® EP-350 is a two component 100% solid Polyurea with superior performance in industrial applications. EP-350 displays extremely fast cure times with excellent adhesions to different subst..