Polymer Property : Modulus of Elasticity = 8.00 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	6.00 - 8.00 GPa	870 - 1160 ksi	Injection; ISO 527
Raschig Group 6552 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
Modulus of Elasticity	6.00 - 8.00 GPa	870 - 1160 ksi	Compression; ISO 527
Raschig Group DECAL® 666/8 Phenolic Glass-fiber reinforced phenolic molding compound with mineral fillers. High heat resistance, reduced mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This prod..
Modulus of Elasticity	6.00 - 8.00 GPa	870 - 1160 ksi	Compression; ISO 527
Raschig Group DECAL® 666/8/2B Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowe..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPAS® 2010 MF Melamine Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection; ISO 527
Raschig Group MELOPAS® 6605 MP Melamine Cellulose reinforced Melamine molding compound. Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding be..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPLAS® 150 MF Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPLAS® 152 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPLAS® 181 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. High surface hardness, good electrical properties, good mechanical strength, high UV and heat resistanc..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPLAS® 183 MF Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection; ISO 527
Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	ISO 527
Raschig Group RALUPOL® 2200 UP Polyester Organically filled polyester molding compound. Low post-shrinkage, good electrical values and mechanical properties, high surface quality and good color stability (non-yellowing). This product meets..
Modulus of Elasticity	5.50 - 8.00 GPa	798 - 1160 ksi	Average value: 7.05 GPa Grade Count:6
Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 20% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 20% Glass Reinforced". Each property range of values reported is minimum and maximum values..
Modulus of Elasticity	6.00 - 8.00 GPa	870 - 1160 ksi	Average value: 7.14 GPa Grade Count:7
Overview of materials for Phenolic, Novolac, Fabric Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Fabric Filled". Each property range of values reported is minimum and maximum values ..
Modulus of Elasticity	3.10 - 8.00 GPa	450 - 1160 ksi	Average value: 5.19 GPa Grade Count:8
Overview of materials for Nylon 66, 10% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Mineral Filled". Specific grades with primary filler content between 5% and 14% are includ..
Modulus of Elasticity	0.485 - 8.00 GPa @Temperature -140 - 250 °C	70.3 - 1160 ksi @Temperature -220 - 482 °F	Average value: 4.72 GPa Grade Count:4
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of..
Modulus of Elasticity	6.55 - 8.00 GPa	950 - 1160 ksi	Average value: 7.31 GPa Grade Count:4
Overview of materials for Nylon 11 with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11 with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are includ..
Modulus of Elasticity	1.36 - 8.00 GPa	197 - 1160 ksi	Average value: 3.09 GPa Grade Count:5
Overview of materials for Nylon 12, Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Graphite Filled". Each property range of values reported is minimum and maximum values of appr..
Modulus of Elasticity	5.00 - 8.00 GPa	725 - 1160 ksi	Injection and Compression; ISO 527
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing ..
Modulus of Elasticity	6.00 - 8.00 GPa	870 - 1160 ksi	Compression; ISO 527
Raschig Group RALUPOL® 8605 UP Polyester Glass fiber reinforced polyester molding compound. Resistant to hydrolysis. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU dire..