Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 195 GPa | 28300 ksi | RT |
Outokumpu 254 SMO® High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |
|||
Modulus of Elasticity | 195 - 210 GPa | 28300 - 30500 ksi | |
Materion Beryllium Nickel Strip - Alloy 360 Hard, 1.5 hr at 950°F Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: 1.5 hrs @ 510ºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation.. |
|||
Modulus of Elasticity | 195 - 210 GPa | 28300 - 30500 ksi | |
Materion Beryllium Nickel Strip - Alloy 360 MH12, Mill Hardened Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation afte.. |
|||
Modulus of Elasticity | 195 - 210 GPa | 28300 - 30500 ksi | |
Materion Beryllium Nickel Strip - Alloy 360 MH6, Mill Hardened Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation afte.. |
|||
Modulus of Elasticity | 195 - 210 GPa | 28300 - 30500 ksi | |
Materion Beryllium Nickel Strip - Alloy 360 MH8, Mill Hardened Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation afte.. |
|||
Modulus of Elasticity | 195 GPa | 28300 ksi | |
Industeel URANUS® B28 High Nickel Super-Austenitic Stainless Steel Description: URANUS® B28 (UR B28) is a super-austenitic stainless steel with very high nickel (31%) and chromium (27%) contents. The molybdenum content is about 3.5%. The alloy is designed for sp.. |
|||
Modulus of Elasticity | 195 - 210 GPa | 28300 - 30500 ksi | |
Materion Beryllium Nickel Strip - Alloy 360 1/2 Hard, 1.5 hr at 950°F Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: 1.5 hrs @ 510ºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation.. |
|||
Modulus of Elasticity | 195 - 210 GPa | 28300 - 30500 ksi | |
Materion Beryllium Nickel Strip - Alloy 360 MH2, Mill Hardened Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation afte.. |
|||
Modulus of Elasticity | 195 - 210 GPa | 28300 - 30500 ksi | |
Materion Beryllium Nickel Strip - Alloy 360 MH4, Mill Hardened Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 99%Stress Relaxation afte.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 204 °C |
28300 ksi @Temperature 399 °F |
heat treated at 1121°C (2050°F) and rapid quenched |
Haynes Hastelloy® C-276 alloy, solution heat treated flat products Hastelloy® C-276 alloy is a nickel-molybdenum-chromium wrought alloy that is a versatile corrosion-resistant alloy. C-276 alloy is an improved wrought version of alloy C in that it usually doesn'.. |
|||
Modulus of Elasticity | 195 GPa | 28300 ksi | |
Latrobe Lescalloy® 13-8 Mo VIM-VAR Precipitation Hardening Stainless Steel Lescalloy 13-8 Mo VIM-VAR is a precipitation hardening martensitic stainless steel offering excellent fracture toughness and transverse mechanical properties coupled with the resistance to stress-co.. |
|||
Modulus of Elasticity | 195 GPa | 28300 ksi | |
Specialty Materials 5521 Boron Epoxy Prepreg Tape Specialty Materials' 5521 is a highly advanced prepreg tape, combining Specialty Materials' 4.0 or 5.6 mil boron filament with a tough, rigid, epoxy resin. Performing at temperatures up to 350°F,.. |
|||
Modulus of Elasticity | 195 GPa | 28300 ksi | 200 HB. |
Assab Steels 760 Machinery Steel ASSAB 760 is an easily machinable carbon steel characterized by: Good machinabilityGood mechanical strengthASSAB 760 is primarily intended to be used in the as-delivered condition. It is only to be .. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, 20% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Modulus of Elasticity | 195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |