Polymer Property : Modulus of Elasticity = 27000 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Elasticity 186 GPa

@Temperature 200 °C
27000 ksi

@Temperature 392 °F
Outokumpu 4301 Cr-Ni Austenitic Stainless Steel
General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll..
Modulus of Elasticity 186 GPa

@Temperature 200 °C
27000 ksi

@Temperature 392 °F
Outokumpu 4306 Cr-Ni Austenitic Stainless Steel
General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll..
Modulus of Elasticity 186 GPa

@Temperature 200 °C
27000 ksi

@Temperature 392 °F
Outokumpu 4307 Cr-Ni Austenitic Stainless Steel
General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll..
Modulus of Elasticity 186 GPa

@Temperature 200 °C
27000 ksi

@Temperature 392 °F
Outokumpu 4311 Cr-Ni Austenitic Stainless Steel
Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms..
Modulus of Elasticity 186 GPa

@Temperature 200 °C
27000 ksi

@Temperature 392 °F
Outokumpu 4432 Cr-Ni-Mo Austenitic Stainless Steel
General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r..
Modulus of Elasticity 186 GPa

@Temperature 200 °C
27000 ksi

@Temperature 392 °F
Outokumpu 4541 Cr-Ni Austenitic Stainless Steel
Good corrosion resistance and weldable. Resistant to sensitization.Applications: Welded screensFurnace beltsCatalytic converter meshAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (C..
Modulus of Elasticity 186 GPa
27000 ksi
H.C. Starck NRC® 5N (UNS R05200) Electron Beam Melted Tantalum
Applications: NRC® ETA Tantalum metal products are used where purity and or ductility of the tantalum metal is more important than strength or grain size. Consequently, their primary applicatio..
Modulus of Elasticity 186 GPa

@Temperature 204 °C
27000 ksi

@Temperature 400 °F
Latrobe LSSâ„¢ H12 Hot Work Tool Steel (ASTM H12)
TLS H12 hot work tool steel is a 5% chromium, general-purpose hot work steel that is characterized by excellent impact toughness. It contains less vanadium than the widely-used H13 hot work tool ste..
Modulus of Elasticity 186 GPa

@Temperature 204 °C
27000 ksi

@Temperature 400 °F
Latrobe LSSâ„¢ H13 PQ Hot Work Tool Steel
TLS H13 PQ is Premium Quality H13 hot work steel that is designed to meet the highest quality standards in the die casting industry, and to excel in the most demanding hot work tooling applications...
Modulus of Elasticity 186 GPa

@Temperature 204 °C
27000 ksi

@Temperature 400 °F
Latrobe LSSâ„¢ H13 Tool Steel (ASTM H13)
TLS H13 tool steel is a versatile chromium-molybdenum hot work steel that is widely used in hot work and cold work tooling applications. The hot hardness (hot strength) of H13 resists thermal fatigu..
Modulus of Elasticity 186 GPa
27000 ksi
H.C. Starck Ultra 76 Alloy (Ta 2.5%W)
Benefits: Significantly improved corrosion resistance in HCl and H2SO4 acids.Minimized hydrogen embrittlement rates compared to standard NRC®76Up to 100 times lower in HCl acidUp to 10 times low..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F)
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F)
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F)
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F)
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Modulus of Elasticity 186 GPa
27000 ksi
Carpenter 20-Mo6® Stainless Steel, Strip
Data provided by Carpenter Technology Corporation.This is an austenitic stainless steel which is resistant to corrosion in hot chloride environments with low pH. It has good resistance to pitting, ..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, 30% cold reduction
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Modulus of Elasticity 186 GPa

@Temperature 400 °C
27000 ksi

@Temperature 752 °F
Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..