- Polymer Property : Modulus of Elasticity = 26700 ksi
Polymer Property : Modulus of Elasticity = 26700 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 50% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 50% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 1 hour at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 400 °C |
26700 ksi @Temperature 752 °F |
|
| Assab Steels ASP 23 Cold Work Steel ASP 23 is a chromium-molybdenum-tungsten-vanadium alloyed high speed steel which is characterized by:High wear resistance (abrasive profile)High compressive strengthVery good through-hardening prope.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy plate, 16000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||