Polymer Property : Modulus of Elasticity = 218 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy sheet Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 0% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 10% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 10% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 10% cold reduction, 980Â°C (1800Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 20% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 20% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 20% cold reduction, 980Â°C (1800Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 30% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 30% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 40% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 40% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 40% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 40% cold reduction, 980Â°C (1800Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 50% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 50% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 50% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 50% cold reduction, 980Â°C (1800Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, sheet, 100 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, sheet, 100 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, sheet, 100 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, sheet, 1000 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, sheet, 1000 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, sheet, 1000 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, sheet, 32 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, sheet, 32 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 30% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	218 GPa	31600 ksi	RT
Haynes 214Â® alloy, 30% cold reduction, 980Â°C (1800Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..