Polymer Property : Modulus of Elasticity = 1890 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Elasticity 11.0 - 13.0 GPa
1600 - 1890 ksi
Injection and Compression; ISO 527
Raschig Group EPOXIDUR® 3581 S ZC EP Epoxy Molding Compound
Inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very good sealing connection on ..
Modulus of Elasticity 10.0 - 13.0 GPa
1450 - 1890 ksi
Compression; ISO 178
Raschig Group RALUPOL® 4385 UP
Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very high arc resistance, very high mechanical values. This product meets the allowed upper limits for heavy..
Modulus of Elasticity 6.27 - 13.0 GPa
909 - 1890 ksi
Average value: 9.82 GPa Grade Count:4
Overview of materials for PCT, 40% Glass Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "PCT, 40% Glass Reinforced". Specific grades with glass content between 35% and 44% are included. Each pr..
Modulus of Elasticity 1.93 - 13.0 GPa
280 - 1890 ksi
Average value: 4.01 GPa Grade Count:7
Overview of materials for Polyphenylene Ether, PTFE Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, PTFE Filled". Each property range of values reported is minimum and maximum values ..
Modulus of Elasticity 8.69 - 13.0 GPa
1260 - 1890 ksi
Average value: 10.5 GPa Grade Count:3
Overview of materials for Polycarbonate, Carbon + Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon + Glass Fiber Reinforced". Each property range of values reported is minimum and m..
Modulus of Elasticity 10.0 - 13.0 GPa

@Temperature 80.0 - 80.0 °C
1450 - 1890 ksi

@Temperature 176 - 176 °F
Average value: 11.5 GPa Grade Count:2
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl..
Modulus of Elasticity 0.350 - 13.0 GPa
50.8 - 1890 ksi
Average value: 2.29 GPa Grade Count:251
Overview of materials for Nylon 6, Unreinforced
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri..
Modulus of Elasticity 2.333 - 13.0 GPa

@Temperature -40.0 - 230 °C
338.4 - 1890 ksi

@Temperature -40.0 - 446 °F
Average value: 7.20 GPa Grade Count:8
Overview of materials for Polyphthalamide (PPA), Glass Fiber 40%
This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Glass Fiber 40%". Specific grades with glass content between 35% and 44% are included. ..
Modulus of Elasticity 0.100 - 13.0 GPa
14.5 - 1890 ksi
Average value: 1.50 GPa Grade Count:209
Overview of materials for Polypropylene Copolymer
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene Copolymer". Each property range of values reported is minimum and maximum values of approp..