- Polymer Property : Modulus of Elasticity = 184 GPa
Polymer Property : Modulus of Elasticity = 184 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 0% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 600 °C |
26700 ksi @Temperature 1110 °F |
|
| Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 25.4 mm thick bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 50% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 6.4 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, all-weld metal, GMAW weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, plate, 16000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 538 °C |
26700 ksi @Temperature 1000 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 0.71 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 184 GPa @Temperature 500 °C |
26700 ksi @Temperature 932 °F |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||