Polymer Property : Modulus of Elasticity = 170 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Elasticity 170 - 190 GPa
24700 - 27600 ksi
Youngs Modulus
MMCC Al/Al2O3 Particulate Aluminum Matrix Composite
Cast, discontinuously reinforced aluminum matrix composite. May be fabricated by vacuum infiltration of the ceramic preform.Data provided by the manufacturer, Metal Matrix Cast Composites (MMCC).
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 700 °C
24700 ksi

@Temperature 1290 °F
Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F)
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity 170 GPa

@Temperature 538 °C
24600 ksi

@Temperature 1000 °F
Latrobe Lescalloy® Jethete M-152 ESR 2.25" RD High Strength Stainless Steel
LESCALLOY JETHETE M-152 ESR is a nitrogen bearing, hardenable 12% chromium stainless steel intended for various structural components requiring high strength and good oxidation resistance up to 800Â..
Modulus of Elasticity 170 GPa
24700 ksi
Filament property, in tension
Cytec Thornel® Mat VMC Carbon Fiber
Data provided by the manufacturer, Amoco Performance Products, Inc.Prepared by sectioning mat VMA into cubes ~ 0.5x0.5x1.0 in. VMC can be heterogeneously dispersed in matrix materials and thus enha..
Modulus of Elasticity 170 GPa
24700 ksi
Filament property, in tension
Cytec Thornel® Mat VMD Carbon Fiber
Data provided by the manufacturer, Amoco Performance Products, Inc.Form of mat VMA with shorter fibers for injection molding. Fiber lengths average 400 µm - adequate for good property improvement...
Modulus of Elasticity 170 GPa

@Temperature 400 °C
24700 ksi

@Temperature 752 °F
Assab Steels VANADIS 4 Cold Work Steel
VANADIS 4 is a chromium-molybdenum-vanadium alloyed steel which is characterized by:High wear resistanceHigh compressive strengthVery good through-hardening propertiesVery good toughnessExcellent di..
Modulus of Elasticity 170 GPa

@Temperature 649 °C
24700 ksi

@Temperature 1200 °F
ATI Allegheny Ludlum AL 625HP™ Stainless Steel
Nickel-based superalloy. Characteristics:exceptional fatigue resistance, excellent resistance to oxidation and corrosion, outstanding strength and toughness over a range of temperatures from cryogen..