Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 8.20 GPa | 1190 ksi | ISO 178 |
Addiplast Addinyl A2 V30 Nylon 66, 30% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||
Modulus of Elasticity | 8.20 GPa | 1190 ksi | ISO 527 |
BASF Ultramid® B3G8 BK00564 40% Glass Filled PA6 (Conditioned) Ultramid B3G8 BK00564 is a 40% glass filled, pigmented black, injection molding PA6 grade. |
|||
Modulus of Elasticity | 8.20 GPa | 1190 ksi | ISO 178 |
Addiplast Addinyl A2 ZV30 Nylon 66, 30% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast. |
|||
Modulus of Elasticity | 8.20 GPa | 1190 ksi | ISO 527-2 |
BASF Ultradur B 4406 G4 PBT Description: Is a PBT, flame-retardant injection-molding grades, with 20% glass fibers, for parts requiring enhanced fire resistance, e.g. plug-and-socket connectors, housings, coil formers and ligh.. |
|||
Modulus of Elasticity | 8.20 - 23.0 GPa @Temperature 60.0 - 150 °C |
1190 - 3340 ksi @Temperature 140 - 302 °F |
Average value: 14.6 GPa Grade Count:1 |
Overview of materials for Nylon 66, 40% Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Carbon Fiber Filled". Specific grades with carbon fiber content between 35% and 44% are in.. |
|||
Modulus of Elasticity | 8.20 GPa | 1190 ksi | ISO 178 |
Addiplast Addinyl B2 V30 Nylon 6, 30% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||
Modulus of Elasticity | 8.20 GPa | 1190 ksi | ISO 178 |
Addiplast Addinyl B2 ZV30 Nylon 6, 30% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast. |