Polymer Property : 100% Modulus = 0.696 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
100% Modulus	0.00480 GPa	0.696 ksi	Press-cured 5 minutes at 190°C
DuPont Vamac® DP Sartomer 350 Coagent Test Compound Vamac® DP is an ethylene acrylic dipolymer elastomer. Its general performance characteristics are similar to those of the Vamac® terpolymers, including:Good oil and chemical resistanceHigh temper..
100% Modulus	0.00480 GPa	0.696 ksi	ASTM D412
Lubrizol ESTANE® 58300 Ether Based Thermoplastic Polyurethane Features: Good physical properties, hydrolysis resistance, low temperature performance and abrasion with a wide processing window for extrusion.Uses: Blown and flat die/cast film extrusion, Injectio..
100% Modulus	0.00480 GPa	0.696 ksi	ASTM D412
Lubrizol ESTANE® 58370 Ether Based Thermoplastic Polyurethane Features: Halogenated flame retardant compoundUses: Extrusion – Wire and cable and general application where flame retardant properties are neededAvailable in Americas, Europe, Middle East, Africa,..
100% Modulus	0.00480 GPa	0.696 ksi	ASTM D412
Lubrizol ESTANE® 58881 Ether Based Thermoplastic Polyurethane Features: Very high tensile strength, excellent low temperature flexibility, and superior abrasion and cut resistanceUses: Extrusion – Wire and cable, Hose and tube & General purposeAvailable in Am..
100% Modulus	0.00480 GPa	0.696 ksi
Lubrizol Estane® 54611 Polyester-Based Thermoplastic Polyurethane Feature: Facilitates to produce high coating weight in one pass high production speed. Broad process window and transparent spherical pellets.Uses: Melt roll coated fabrics and unsupported foils.Av..
100% Modulus	0.00480 GPa	0.696 ksi	ASTM D412/D638
Lubrizol ESTANE® 5714 Ether Based Thermoplastic Polyurethane Features: Low Temperature Flexibility, Excellent Abrasion, Fungal, and Chemical Resistance, and Hydrolytic Stability. Adhesives can be applied from solution or extruded as a melt coating. The resin ..
100% Modulus	0.00480 GPa	0.696 ksi	Press cure 10 minutes@ 177°C
3M Dyneon™ FPO 3740 Fluoroelastomer 3M™ Dyneon™ FPO 3740 is a peroxide curable fluoroelastomer terpolymer containing 69.5 wt% fluorine. FPO 3740 can be used in compression, transfer or injection molding, and extrusion processes. Fea..
100% Modulus	0.00480 GPa	0.696 ksi	Press Cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 200°C; ASTM D412
3M Dyneon™ PFE 80Z Peroxide Cure Perfluoroelastomer 3M™ Dyneon™ Peroxide Cure Perfluoroelastomer PFE 80Z is a technically advanced peroxide curable perfluoroelastomer. This product is designed to have improved acid resistance and lower metal ion ex..
100% Modulus	0.00480 GPa	0.696 ksi	500 mm/min, measured parallel to flow; ISO 37
AlphaGary Evoprene™ GF 6257 Automotive Thermoplastic Elastomer Evoprene™ GF is a hydrogenated styrene block copolymer based thermoplastic elastomer created for the automotive industry. It is specially formulated to have very low fogging characteristics suitab..
100% Modulus	0.00480 GPa	0.696 ksi	500 mm/min, measured parallel to flow; ISO 37
AlphaGary Evoprene™ LF 6156 Automotive Thermoplastic Elastomer Evoprene™ LF is a hydrogenated styrene block copolymer based thermoplastic elastomer created for the automotive industry. It is specially formulated to have very low fogging characteristics suitab..
100% Modulus	0.00480 GPa	0.696 ksi	ASTM D412-80
DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound (d Carbon black compound with 100 parts Hypalon; 27.8 parts sublimed litharge dispersion; 55 parts carbon black; 55 parts aromatic process oil; 0.5 parts MTBS; and 2 parts Tetrone® A rubber accelerato..