Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 310 MPa | 45000 psi | |
Mykroy/Mycalex MM 400 Machining Grade Glass-bonded Mica Composite Natural mica filler. Does not burn. Good radiation resistance (3 x 10^10 Rads-Cobalt).This ceramoplastic material is a versatile and efficient insulating material designed to meet the exacting dem.. |
|||
Compressive Strength | 310 MPa | 45000 psi | |
Mykroy/Mycalex MM 451 Molding Grade Glass-bonded Mica Composite Natural mica filler. Does not burn. ROHS Compliant.This ceramoplastic material is a versatile and efficient insulating material designed to meet the exacting demands of technical markets, worldwid.. |
|||
Compressive Strength | 310 MPa | 45000 psi | |
Mykroy/Mycalex MM 501 Molding Grade Glass-bonded Mica Composite Natural mica filler. Does not burn. ROHS Compliant.This ceramoplastic material is a versatile and efficient insulating material designed to meet the exacting demands of technical markets, worldwide.. |
|||
Compressive Strength | 310 MPa | 45000 psi | ASTM D695 |
Owens Corning Glass Fiber Reinforced Epoxy (Filament Wound), 80 wt.% glass Epoxies are highly resistant to water, alkalis and organic solvents. Although standard epoxies have only a fair resistance to acids and oxidizing agents, they can be formulated for better resistance.. |
|||
Compressive Strength | 310 MPa | 45000 psi | |
Pyrotek TS-103 Thermoset Electrical Insulation Product (Nema Grade: G-3) Glass reinforcement, Phenolic resin, Natural color. Good heat resistance. Excellent mechanical and machining properties.ApplicationsSuperstructure support pads Bus bar insulators Pot cradle insula.. |
|||
Compressive Strength | 310 MPa | 45000 psi | |
Pyrotek MCX-40 Insulating Board MCX-40 is a bonded-mica composite for use in glass contact applications. Its high operating temperature, low porosity, and low thermal conductivity make it ideal for all areas of hot glass transfer.. |
|||
Compressive Strength | 310 MPa @Thickness 12.7 mm |
45000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP159 Synthetic Fabric
(discontinued **) Description: Woven aramid fiber fabric combined with high temperature phenolic resin. With a proper post baking procedure, NP159 will withstand continuous operation at 200° C. Material becomes brit.. |
|||
Compressive Strength | 310 MPa @Thickness 12.7 mm |
45000 psi @Thickness 0.500 in |
ASTM D695 |
Industrial Laminates/Norplex NP611 Paper Base Laminate Description: Hot punching general-purpose phenolic grade. Mechanical properties approach those of NP610 with improved electrical properties and moisture resistance.Thickness Tested: 0.062", 0 125" a.. |
|||
Compressive Strength | 310 MPa @Treatment Temp. 50.0 °C, Time 3600 sec |
45000 psi @Treatment Temp. 122 °F, Time 1.00 hour |
ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola G-Etronax SI Silicone, Glass Fabric Reinforcement, White, Sheets Description: Electrical and electrotechnical applications. Suitable as high-frequency insulation on account of its dielectric loss. Used as, among other things, an insulation material in large induc.. |
|||
Compressive Strength | 310 MPa @Thickness >=5.00 mm |
45000 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola Etronit 201M Phenolic, Paper Reinforcement, Dark Brown, Sheets Description: Grade with high mechanical properties but the lowest electrical properties of all Etronit types. Used for mechanical applications.Applications: Dies, topplates and back-up plates for dr.. |
|||
Compressive Strength | 310 MPa | 45000 psi | |
Aremco AREMCOLOX™ 502-400 Machinable Glass Ceramic High dielectric and mechanical strength. For high voltage insulators, coil forms, soldering fixtures, arc barriers. Readily machined, no firing required. Plates from 1/8" to 1" thick; rods from 1.. |
|||
Compressive Strength | 310 MPa | 45000 psi | ASTM D695 |
Premix Premi-Glas® 1282-32 VE Glass Reinforced Vinyl Ester SMC
(discontinued **) Description: Premi-Glas® 1282-32 VE SMC is an enhanced high strength glass reinforced vinyl ester molding compound formulated for under-the-hood automotive applications.
Key features and benefi.. |
|||
Compressive Strength | 310 MPa | 45000 psi | ISO 604 |
Sumitomo Bakelite North America RX® 680 Fiberglass and Glass Reinforced Phenolic RX 680 is a fiberglass and glass bead filled phenolic molding compound, with good dimensional stability and good strength at elevated temperatures.Information provided by Sumitomo Bak North America,.. |
|||
Compressive Strength | 310 MPa @Thickness >=5.00 mm |
45000 psi @Thickness >=0.197 in |
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
Elektro-Isola Etronit 201M S Phenolic, Paper Reinforcement, Black, Sheets Description: Grade with high mechanical properties but the lowest electrical properties of all Etronit types. Used for mechanical applications. The material is black throughout. Used where the mecha.. |
|||
Compressive Strength | 310 MPa | 45000 psi | ASTM D695 |
Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC
(discontinued **) Description: Premi-Glas® 1281-32 VE SMC is a high strength glass reinforced vinyl ester sheet molding compound formulated for under-the-hood automotive applications. Key features and benefits: Desi.. |