Polymer Property : Compressive Strength = 38000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Compressive Strength 262 MPa

@Temperature 23.9 °C
38000 psi

@Temperature 75.0 °F
Dry; ASTM D695
Park Electrochemical Nelcote® V-341 Polybutadiene Prepreg, 120 E-Glass Reinforced
Nelcote® V-341 is Polybutadiene resin system designed to provide excellent electrical properties in demanding airborne, shipboard, and undersea applications.Key Features and Benefits:Extremely low ..
Compressive Strength 262 MPa
38000 psi
Pyrotek TS-102 Thermoset Electrical Insulation Product (Nema Grade: X)
Paper reinforcement, Phenolic Resin, Natural Color. High mechanical strength. Electrical properties are secondary.ApplicationsSuperstructure support pads Bus bar insulators Pot cradle insulators E..
Compressive Strength 262 MPa
38000 psi
Pyrotek TS-83 Thermoset Electrical Insulation Product (Nema Grade: LE)
Linen reinforcement, Phenolic resin, Tan / Black color. Good electrical and high mechanical strength. Moisture resistant.Information provided by Pyrotek.
Compressive Strength 262 MPa
38000 psi
Performance Alloys MoldStar® 18 (PAS 18) Bronze Mold Alloy
Description: MoldStar® 18 bronze alloy provides good bearing qualities and resistance to wear, abrasion, fatigue, deformation and corrosion.Applications: SlidesGibsWear PlatesMold Locking DevicesSl..
Compressive Strength 262 MPa
38000 psi
LE Phenolic Laminate
Linen based phenolic provides more mechanical strength than paper grades and has a finer surface with better machinability. This material is used for gears, pinions, bearings, bushings, and many st..
Compressive Strength 262 MPa
38000 psi
XXX Phenolic Laminate
Paper based phenolic provides low cost electrical and mechanical properties. It is widely used for switchboards, panel boards, insulating washers, and intricate punched parts.Information provided b..
Compressive Strength 262 MPa

@Thickness 3.17 mm
38000 psi

@Thickness 0.125 in
Flatwise
Industrial Laminates/Norplex MC223 Cotton Fabric
Description: Grade MC223 is a medium weave cotton phenolic composite that is specifically formulated to meet MIL-P-18324.Typical applications include pintle and stave-type bearings for rudder shafts..
Compressive Strength 262 MPa

@Thickness 3.17 mm
38000 psi

@Thickness 0.125 in
Flatwise
Industrial Laminates/Norplex MC320LE Cotton Fabric
Description: Grade MC320LE is a fine weave bleached cotton phenolic composite that has excellent machining characteristics and low moisture absorption. Applications include marine applications, term..
Compressive Strength 262 MPa

@Thickness 12.7 mm
38000 psi

@Thickness 0.500 in
ASTM D695
Industrial Laminates/Norplex NP315 Cotton Fabric
Description: Canvas phenolic laminate with graphite added as a solid lubricant. This material has improved wear properties under certain conditions. Material is conductive to electricity and should ..
Compressive Strength 262 MPa

@Thickness 12.7 mm
38000 psi

@Thickness 0.500 in
ASTM D695
Industrial Laminates/Norplex NP320 Cotton Fabric
Description: Fine weave (less than 4 ounce/square yard) cotton fabric commonly called linen, combined with phenolic resin to provide better machining than NP310. For smaller and more intricate shape..
Compressive Strength 262 MPa

@Thickness 12.7 mm
38000 psi

@Thickness 0.500 in
ASTM D695
Industrial Laminates/Norplex NP680 Paper Base Laminate
Description: Hot punching grade with electrical properties between NP611 to NP631.Thickness Tested: 0.062", 0.125" & 0.500"
Compressive Strength 262 MPa
38000 psi
ASTM D695
Greene Tweed Arlon® 1260 Polyketone, Carbon Filled
Arlon® 1260 is a carbon-fiber reinforced version of Arlon 1000 featuring the highest modulus and tensile strength of all the Arlon grades. Designers requiring a low coefficient off thermal expan..
Compressive Strength 262 MPa
38000 psi
ASTM D695
Greene Tweed Arlon® 1263 PEEK, Carbon Filled
Arlon® is a tough, high-temperature, semi-crystalline, thermoplastic presenting a unique combination of mechanical, thermal, chemical and electrical properties. Greene, Tweed uses several proprie..
Compressive Strength 262 MPa
38000 psi
ASTM D695
Sumitomo Bakelite North America FM 4004 Fiberglass and Mineral Reinforced Phenolic Novolac
FM 4004 is a fiberglass and mineral reinforced phenolic novolac compound. This compound exhibits excellent dimensional stability and good strength at elevated temperatures, and conforms to the requ..