Polymer Property : Compressive Strength = 32600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Compressive Strength 225 MPa
32600 psi
Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 85 Phenolic Formaldehyde Resin, UL Listed  (discontinued **)
Phenolic molding compound, organically filled, reinforced with cotton fibers, average notched impact strength, UL listed molding compound 1.5 mm/HB (BK, BN).Application areas: Switch covers, rolls, ..
Compressive Strength 225 MPa
32600 psi
Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 2535 Phenolic Formaldehyde Resin, High Surface Quality, Dishwasher Proof  (discontinued **
Phenolic molding compound, inorganically/organically filled, average heat resistant, steam resistant, dish washer proof, high surface quality.Application areas: Fittings for ovens and dishwashers, t..
Compressive Strength 225 MPa
32600 psi
Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 2736 Phenolic Formaldehyde Resin, Improved Electrical Properties, Low Shrinkage, UL Listed &nbs
Phenolic molding compound, inorganically/organically filled, increased tracking resistance, UL listed molding compound 0.46 mm/V-0 (BK, Suffix "H"), 0.81 mm/V-0 (NC, GN, BK), 1.5 mm/V-0 (ALL).Applic..
Compressive Strength 225 MPa
32600 psi
Test specimen flat tested; ISO 604
Hexion Bakelite™ 151733 Phenolic Formaldehyde Resin  (discontinued **)
Phenolic molding compound, mainly organically filled, standard molding compound for normal stress.Application areas: Contact strips.Information provided by Bak AGBak AG became a part of Hexion in 20..
Compressive Strength 225 MPa
32600 psi
Test specimen flat tested; ISO 604
Hexion Bakelite™ X22 Phenolic Formaldehyde Resin, UL Listed  (discontinued **)
Phenolic molding compound, mainly organically filled, UL listed molding compound 3.0 mm/V-0 (BN, BK).Application areas: Pot handles, operating controls, electrical isolators, housing parts.Informati..
Compressive Strength 225 MPa

@Temperature 23.0 °C
32600 psi

@Temperature 73.4 °F
EN ISO 604
Ensinger TECASINT 3022 Polyimide, Black, 15% Graphite (PI)
TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Compressive Strength 225 MPa
32600 psi
Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 1142 Phenolic Formaldehyde Resin, High Mechanical Strength  (discontinued **)
Phenolic molding compound, inorganically filled, glass fiber reinforced, high dimensional stability, good mechanical properties.Application areas: Insulating flanges, sealings, pulleys.Information p..
Compressive Strength 225 MPa
32600 psi
Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 2560 Phenolic Formaldehyde Resin, High Surface Quality, For Electrostatic Coating, UL Listed &n
Phenolic molding compound, inorganically/organically filled, average heat resistant, high surface quality, lower water absorption than PF 31, minimal distortion, UL listed molding compound 1.5 mm/V-..