Polymer Property : Compressive Strength = 2610 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Compressive Strength 18.0 MPa
2610 psi
1% strain over 1000 hours; ISO.899 DIN.53444
Omnia Plastica Omniamid PA 6 - Akulon 6 - Dry
Semi-crystalline polymer of polyamide obtained by the polymerisation of the caprolactam. Its large popularity is due to both its good overall features as well as its cost-performance relationship. T..
Compressive Strength 18.0 MPa
2610 psi
1% strain over 1000 hours; ISO.899 DIN.53444
Omnia Plastica PC Polycarbonate
This amorphous polymer is commonly used for its high shock resistance even at low temperature. It is not a material recommended for mechanical applications, even if its dimensional stability does ma..
Compressive Strength 18.0 MPa
2610 psi
Pyrotek B-3A REFRACTORY BOARD
Pyrotek B-3A is a high density calcium silicate board specifically designed for demanding applications such as holding furnaces, launder linings and baffle plates. Its high density and superior har..
Compressive Strength 18.0 MPa

@Strain 5.00 %,
Temperature 300 °C
2610 psi

@Strain 5.00 %,
Temperature 572 °F
Pyrotek ISOMAG® 70 Structural Insulation
Isomag® 70 is magnesia silicate based formulation provides insulating properties similar to calcium silicate with good strength and dimensional stability up to 1000°C. ApplicationsTorpedo cars La..
Compressive Strength 18.0 MPa
2610 psi
10% Yield Point; DIN 53454
Fluorseals PTFE Unfilled
Information provided by TEKU GmbH Fluorkunststoffe, a distributor of Fluorseals materials.
Compressive Strength 18.0 MPa
2610 psi
EN 1094-5: 1995
Skamol Group Moler M-EXTRA 'E' Insulating Block
SKAMOL Moler insulating bricks & blocks have the following characteristics: Max. service temperature: Up to 1000°C (1832°F)Back-up insulation Excellent insulating propertiesHigh mechanical str..