Polymer Property : Compressive Strength = 230 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	230 MPa	33400 psi
Pyrotek TS-120 Thermoset Electrical Insulation Product (Nema Grade: GPO-2) Glass reinforcement, Polyester resin, Cream color. Highly flame resistant. Meets UL 94VO.Information provided by Pyrotek.
Compressive Strength	230 MPa	33400 psi	ASTM D695
Sumitomo Bakelite North America EpiallÂ® 2061B-1 Mineral and Glass Filled Electrical Encapsulation Grade Epoxy Epiall 2061B-1 is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability, good electrical insulation properties, and good strength.Information provided by S..
Compressive Strength	230 MPa @Treatment Temp. 150 °C, Time 3600 sec	33400 psi @Treatment Temp. 302 °F, Time 1.00 hour	ISO 604; IEC/EN 60893-2 5.3
Elektro-Isola G-Etronax SI Silicone, Glass Fabric Reinforcement, White, Sheets Description: Electrical and electrotechnical applications. Suitable as high-frequency insulation on account of its dielectric loss. Used as, among other things, an insulation material in large induc..
Compressive Strength	230 MPa @Temperature 23.0 °C, Time 86400 sec	33400 psi @Temperature 73.4 °F, Time 24.0 hour	50% RH, Axial; ISO 604; IEC/EN 61212-2 5.2
Elektro-Isola G-Etronax EP FR Epoxy, Glass Fabric Reinforcement, Light Yellow, Tubes Description: Mechanical, electrical and electronic applications. Extremely high mechanical strength at moderate temperatures. Very good stability of electrical properties when exposed to high relati..
Compressive Strength	>= 230 MPa	>= 33400 psi	Ambient
China-Yixing Longly Refractories Cordierite Ceramics (Heat Resistance Ceramics) LONGLY's cordierite ceramics' main crystal phrase is 2MgO-2Al2O2-5SiO2, this composition has low thermal expansion coefficient and excellent thermal shock resistance. Maximum service temperature is..
Compressive Strength	230 MPa	33400 psi	ISO 604
Brandenburger Heavy Duty Mounting Paste Information provided by Brandenburger Isoliertechnik GmbH&Co.
Compressive Strength	230 MPa	33400 psi	ISO 604
Vyncolit Neopreg Kinel® SK4504 S12 Carbon Reinforced Molding Compound Epoxy based molding compound long carbon fiber reinforced suited for demanding tribologic applications under dry running conditions, exposed to a wide range of temperatures (-100°C up to 150°C)...
Compressive Strength	230 MPa	33400 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 2874 Phenolic Formaldehyde Resin, Low Shrinkage, Improved Electrical Properties, UL Listed, High Mechanical Strength Phenolic molding compound, inorganically filled, glass fiber reinforced, increased mechanical strength, increased temperature stability, low water absorption, good dimensional stability, UL listed m..
Compressive Strength	230 MPa	33400 psi	ASTM D695
Sumitomo Bakelite North America FM 4004F Fiberglass and Mineral Reinforced Phenolic Novolac FM 4004F is a fiberglass and mineral reinforced phenolic novolac compound with improved strength properties over FM 4004. This compound exhibits excellent dimensional stability and good strength at..