Polymer Property : Compressive Strength = 22000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Compressive Strength 124 - 152 MPa
18000 - 22000 psi
ASTM D695
Mar-Bal MB1000-15 Thermoset Polyester Composite Molding Compound
A general purpose material that is easily customized. Designed for Powder Coating and Electrostatic painting.Mar-Bal standard grades can be injection, compression and transfer molded.Information pro..
Compressive Strength 138 - 152 MPa
20000 - 22000 psi
ASTM D695
Mar-Bal MB1000-PC Thermoset Polyester Composite Molding Compound
A general purpose material that is easily customized. Designed for Powder Coating and Electrostatic painting.Mar-Bal standard grades can be injection, compression and transfer molded.Information pro..
Compressive Strength 124 - 152 MPa
18000 - 22000 psi
Bulk Molding Compounds BMC 100 Thermoset Polyester, GP
BMC 100 is a high strength, low shrink general purpose molding compound. It can be supplied in bulk or extruded in pre-weighted slugs. Due to the excellent flow and controlled reactivity, BMC 100 is..
Compressive Strength 124 - 152 MPa
18000 - 22000 psi
Bulk Molding Compounds BMC 102 Glass Filled Thermoset Polyester
BMC 102 is a medium strength, glass fiber reinforced molding compound that meets Ford Specification ESF-M3D56-A. It can be supplied in bulk or extruded in pre-weighed slugs and is well suited for in..
Compressive Strength 110 - 152 MPa
16000 - 22000 psi
Bulk Molding Compounds BMC 304 Automotive Grade Molding Compound
BMC 304 is a low profile, automotive grade molding compound that is suitable for Injection, Compression or Transfer molding operations. BMC 304 can be coated using traditional or electrostatic coati..
Compressive Strength 124 - 152 MPa
18000 - 22000 psi
Bulk Molding Compounds BMC 310 Cosmetic and Appliance Grade Compound
BMC 310 is a cosmetic and appliance grade material with superior heat and stain resistant properties. As with all other BMCI compounds, this Series can be supplied in logs, slugs or bulk.Typical app..
Compressive Strength 124 - 152 MPa
18000 - 22000 psi
Bulk Molding Compounds BMC T15(F) High Strength Grade Molding Compound
BMC T15F is a high strength, low shrink general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC T15F is well suited for injection, transfer or compression molding..
Compressive Strength 138 - 152 MPa
20000 - 22000 psi
Bulk Molding Compounds BMC 1410 Electrical Grade
BMC 1410 is a high-strength electrical grade material with excellent flammability resistance. In most applications, this material is competitive with SMC. Equal performance at a lower cost. Normally..
Compressive Strength 124 - 152 MPa
18000 - 22000 psi
Bulk Molding Compounds BMC 300 Mineral Filled, Glass Reinforced Polyester
BMC 300 is a general purpose, mineral filled, glass fiber-reinforced polyester that is suitable for compression, transfer and stuffer injection molding. Our Granite-X series of molding compounds bel..
Compressive Strength 131 - 152 MPa
19000 - 22000 psi
Bulk Molding Compounds BMC 810 General Purpose Molding Compound
BMC 810 is a general purpose, very high strength compound suitable for compression, transfer and stuffer injection molding. It is characterized by excellent flow and controlled reactivity and is wel..
Compressive Strength 138 - 152 MPa
20000 - 22000 psi
Bulk Molding Compounds BMC SLC 2000 Glass Reinforced Polyester
BMC SLC 2000 is a medium strength, low-cost, glass reinforced polyester compound with adjustable shrinkage. Ideal for circuit breakers, motor switch housings, fuse holders, brush holders, standoff i..
Compressive Strength 129 - 152 MPa
18700 - 22000 psi
Bulk Molding Compounds BMC T40(18)-LS Die Casting Replacement Grade Molding Compound
BMC T40(18)-LS is a low shrink compound designed as a direct replacement for aluminum die casting applications. T40(18)-LS is UL recognized. Excellent mechanical properties and dimensional stabili..