Polymer Property : Compressive Strength = 17500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	121 MPa	17500 psi	ASTM D695
Owens Corning Glass Fiber Reinforced Polystyrene Acrylonitrile (SAN), 20 wt.% glass Polystyrene provides good resistance to alkalis, most organic solvents, weak acids, and household chemicals. It is not recommended for use with strong acids, ketones, esters, and some chlorinated hy..
Compressive Strength	121 MPa	17500 psi	ASTM D695
Solvay Specialty Polymers AvaSpire® AV-742 SL30 Polyaryletherketone (PAEK) (Unverified Data**) AV-742 SL30 is a wear resistant grade of AvaSpire polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wear re..
Compressive Strength	121 MPa	17500 psi	ASTM D695
Solvay Specialty Polymers KetaSpire® KT-851 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-851 resin is a depth-filtered grade of polyetheretherketone (PEEK) specially designed for use in extruded wire insulation coating. KT-851 offers the needed balance of properties and pro..
Compressive Strength	121 MPa	17500 psi	ASTM D695
Solvay Specialty Polymers KetaSpire® KT-851 NL Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-851 NL resin is a depth-filtered grade of polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form and is specially designed for use in extruded wire insulation..
Compressive Strength	121 MPa	17500 psi
SGL Carbon Group EK 204 Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and..
Compressive Strength	121 MPa	17500 psi	ASTM D695
Solvay Specialty Polymers AvaSpireÂ® AV-742 SL30 Polyaryletherketone (PAEK) AV-742 SL30 is a wear resistant grade of AvaSpireÂ® polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to outstanding wea..
Compressive Strength	121 MPa	17500 psi	ASTM D695
Solvay Specialty Polymers KetaSpireÂ® KT-851 NL Polyetheretherketone (PEEK) KetaSpireÂ® KT-851 NL resin is a depth-filtered grade of polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form and is specially designed for use in extruded wire insula..
Compressive Strength	121 MPa	17500 psi	ASTM D695
Solvay Specialty Polymers KetaSpireÂ® KT-851 Polyetheretherketone (PEEK) KetaSpireÂ® KT-851 resin is a depth-filtered grade of polyetheretherketone (PEEK) specially designed for use in extruded wire insulation coating. KT-851 offers the needed balance of properties and..
Compressive Strength	121 MPa	17500 psi
CMT Materials HYTAC® WFT High Temperature, Ultra-Smooth PTFE Impregnated HYTAC-WFT combines the higher temperature, smooth surface properties of HYTAC-WF with PTFE impregnation for low stick surface capability and excellent material distribution. The result is a syntact..
Compressive Strength	121 MPa	17500 psi	Crosswise; ASTM D635
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 3/16" to 1/4" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	121 MPa	17500 psi	Crosswise; ASTM D635
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 3/8" to 1" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	121 MPa	17500 psi	ASTM D695
Owens Corning Glass Fiber Reinforced Polyphenylene Oxide (PPO), 20 wt.% glass Polyphenylene Oxide provides excellent resistance to aqueous media. It is softened by aromatic hydrocarbons. Data provided by the manufacturer, Owens Corning.