Polymer Property : Tensile Strength = 95.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	95.0 MPa	13800 psi	ISO 527
Panjin Zhongrun Chemerize 012P High Viscosity CoPEEK Information provided by Bieglo Gmbh.
Tensile Strength	95.0 MPa	13800 psi	at Yield; ISO 527-1/-2
Quadrant EPP Nylatron® GS PA 6 + MoS2, extruded (ISO Data) The addition of MoS2 renders this material somewhat stiffer, harder and dimensionally more stable than Ertalon 66 SA, but results in some loss of impact strength. The nucleating effect of the molybd..
Tensile Strength	95.0 MPa	13800 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers KetaSpire® KT-820 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpire PEEK is produced to the highest industry standards and is characteriz..
Tensile Strength	95.0 MPa	13800 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers KetaSpire® KT-820 NL Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-820 NL is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpire PEEK is produced to the highest industry standard..
Tensile Strength	95.0 MPa	13800 psi	ISO 527
Panjin Zhongrun Chemerize 012G High Viscosity CoPEEK Information provided by Bieglo Gmbh.
Tensile Strength	95.0 MPa	13800 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers KetaSpireÂ® KT-820 NL Polyetheretherketone (PEEK) KetaSpireÂ® KT-820 NL is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpireÂ® PEEK is produced to the highest industry ..
Tensile Strength	95.0 MPa	13800 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers KetaSpireÂ® KT-820 Polyetheretherketone (PEEK) KetaSpireÂ® KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpireÂ® PEEK is produced to the highest industry standards and is cha..
Tensile Strength	95.0 MPa	13800 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers KetaSpireÂ® KT-XXXX Polyetheretherketone (PEEK) KetaSpireÂ® KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpireÂ® PEEK is produced to the highest industry standards and is cha..
Tensile Strength	95.0 MPa	13800 psi	ASTM D4894
Saint-Gobain FluoroloyÂ® A22 High Performance Seal Material High modulus with excellent high-temperature resistance; Abrasion resistant; Chemically Inert; Recommended for back-up rings and for special applications. Information provided by Saint-Gobain P..
Tensile Strength	95.0 MPa @Thickness >=1.50 mm	13800 psi @Thickness >=0.0591 in	24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Elektro-Isola Etronit IV Phenolic, Paper Reinforcement, Yellow, Sheets Description: Grade for mechanical electrotechnical and high frequency purposes. Tropical grade, well suited for areas where high air humidity can be expected. Suitable as high-frequency insulation o..
Tensile Strength	95.0 MPa	13800 psi	ISO 527
Azoty Tarnow™ Tarnamid® T-27 GF10 MX6 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grade, reinforced with 10% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning, good surface quality.T..
Tensile Strength	95.0 MPa @Strain 4.00 %, Temperature 0.000 °C	13800 psi @Strain 4.00 %, Temperature 32.0 °F	50 mm/min; ISO 527-2
BASF Elastollan R 3000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength	95.0 MPa	13800 psi	cond.; ISO 527
Azoty Tarnow™ Tarnamid® T-27 GF25 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 25% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning..