Polymer Property : Tensile Strength = 65.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Premix Premi-Glas® 1261-28 VE Glass Reinforced Vinyl Ester TMC Description: Premi-Glas® 1261-28 VE is a glass reinforced vinyl ester molding compound designed for automotive under the hood applications. Key features and benefits: Excellent thermal stability an..
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Premix Premi-Glas® 2200-25 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2200-25 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal ..
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Premix Premi-Glas® 2203-25 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2203-25 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal ..
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Premix Premi-Glas® 2203-25 CR-SX-HT Fiberglass Reinforced Thermoset SMC Premi-Glas® 2203-25 CR-SX-HT is a fiberglass reinforced thermoset sheet molding compound for electrical and flame retardant applications.Key features and benefits are:Enhanced product for higher UL..
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Premix Premi-Glas® 2204-25 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2204-25 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal ..
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Premix Premi-Glas® 2205-25 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2205-25 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal ..
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Premix Premi-Glas® 2207-20 CR-SX Fiberglass Reinforced Thermoset SMC Premi-Glas® 2207-20 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical, flame retardant and HVAC applications.Key features and benefits are:Non-Halogen FR technology f..
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Premix Premi-Glas® 2243-24 CR-SX Fiberglass Reinforced Thermoset Thick Molding Compound Premi-Glas® 2243-24 CR-SX is a fiberglass reinforced thermoset thick molding compound for electrical and flame retardant applications.Key features and benefits are:TMC compounding process preserves..
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Premix Premi-Glas® 3200-25 Fiberglass Reinforced SMC Description: Premi-Glas® 3200-25 is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal and di..
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Kolon KOCETALÂ® K500 Standard Grade Acetal Resin General injection molding grade. Easy flow grade for hard-to fill molds and mechanical thin-wall parts.Applications: General injection molding products.Information provided by API-Kolon.
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Kolon KOCETALÂ® K700BK Colored Grade Acetal Resin Colored, low viscosity grade.Applications: Thin products, improved appearance.Information provided by API-Kolon.
Tensile Strength	65.0 MPa	9430 psi	ASTM D638
Kolon KOCETALÂ® TC701 Mineral Reinforced Acetal Resin Talc reinforced, improved dimensional stability. Applications: Products for high stiffness, dimensional precision. Information provided by API-Kolon.
Tensile Strength	65.0 MPa	9430 psi	ISO 527
Lucite International DiakonÂ® TD510 Toughened Acrylic Compound The DiakonÂ® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness.The grades in the DiakonÂ® series can be processed by..
Tensile Strength	65.0 MPa	9430 psi	DIN 53455
Isoflon POM C Polyacetal C Good optical propertiesHigh UV resistanceAbsorbs little moistureInformation provided by Isoflon.
Tensile Strength	>= 65.0 MPa	>= 9430 psi	GB/T 1040.2-2006
Sichuan Deyang HatonÂ® hc Polyphenylene Sulfide Resin Fiber gradeInformation provided by Sichuan Deyang Chemical Co., LTD
Tensile Strength	65.0 MPa	9430 psi	50 mm/min; ISO 527-1
Sax Polymers SAXAMID 136F3Q32 Nylon 6, 15% Glass Fiber SAXAMID 136F3Q32 is a high-impact-modified polyamide 6 injection-molding-grade reinforced with 15% glass fibers with very high impact properties. Beside the high impact strength at low temperatures ..
Tensile Strength	65.0 MPa	9430 psi	dry; ISO 527
Ter Hell Plastic Terez® PA 6 7750 TK Polyamide 6 Description: Medium viscosity, high impact modified standard grade PA 6, with crystallization accelerator and good flowability.Application: For molding parts with high impact stress.Information pr..
Tensile Strength	65.0 MPa	9430 psi	cond.; DIN 53 455
Hippe PA 46 Nylon 46 PA 46 is primarily used in higher temperature ranges where stiffness, creep resistance, continuous heat stability and fatigue strength are required. Therefore PA 46 is suitable for high quality app..
Tensile Strength	65.0 MPa	9430 psi	DIN 53 455
Hippe PC Polycarbonate Hard, stiff, very good impact properties with a wide range of temperature (to -100°C). High stability of shape under heat. Clear with own slight yellowish color. Low water absorption, weather-re..
Tensile Strength	65.0 MPa	9430 psi	DIN 53 455
Hippe POM Copolymer Polyacetals are particularly suitable for the manufacture of precision and technical components, bushing, spring elements, housing components, sliding elements, chains, curve discs, bearing, running..
Tensile Strength	65.0 MPa	9430 psi	50 mm/min; ISO 37
BASF Elastollan R 2005/1 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength	65.0 MPa	9430 psi	50 mm/min; ISO 37
BASF Elastollan R 2006 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength	65.0 MPa @Strain 2.00 %, Temperature 0.000 °C	9430 psi @Strain 2.00 %, Temperature 32.0 °F	50 mm/min; ISO 527-2
BASF Elastollan R 3000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength	65.0 MPa	9430 psi	50 mm/min; ISO 37
BASF Elastollan R 3001 15% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength	65.0 MPa	9430 psi	cond.; ISO 527
Azoty Tarnow™ Tarnamid® T-27 GF15 Polyamide 6 - Glass Fiber Reinforced 15% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High..
Tensile Strength	65.0 MPa	9430 psi	50 mm/min; ISO 37
BASF Elastollan R 2000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..