Polymer Property : Tensile Strength = 6090 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	42.0 MPa @Thickness 0.0500 mm	6090 psi @Thickness 0.00197 in	ASTM D882-02
NeXolve Clear Optionox® Polyimide Film/Coating Highly UV durable with excellent weatherability and stability to ozone.Optinox® films and coatings are highly UV durable and exhibit excellent weathering durability, including very high stability ..
Tensile Strength	42.0 MPa	6090 psi	ISO 527
FKuR Kunststoff Bio-FlexÂ® F 6513 Compostable PLA Blend The BIO-FLEXÂ® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEXÂ® does not contain any sta..
Tensile Strength	42.0 MPa	6090 psi	ASTM D412
GRECO ISOTHANE 2095A Poly(caprolactone)ester TPUÂ Resin ISOTHANE 2000 series products are polyester poly(caprolactone)ester based thermoplastic polyurethane. They exhibit excellent toughness, abrasive resistance, solvent resistance, and hydrolysis stabi..
Tensile Strength	42.0 MPa	6090 psi	ASTM D638
KYDEXÂ® 152WG Capped Wood Grain Thermoplastic Sheet Features:Super tough, durableHigh extensibility, rigidity, abrasion resistance and fire retardancyMore rigid than most thermoplastics, parts deform less when loadedOutstanding resistance to breakage..
Tensile Strength	42.0 MPa	6090 psi	ASTM D638
KYDEXÂ® 311 Co-Extruded High Impact Fire-Rated Thermoplastic Sheet Features:Color-matched cap, black or off-white substrateThickness ranging from 1.5 mm to 8.9 mmToughness and durabilityEasy to form with good part definitionChemical resistantFire retardantExcellent..
Tensile Strength	42.0 MPa	6090 psi	ASTM D638
KYDEXÂ® 311 MB Co-Extruded High Impact Fire-Rated Thermoplastic Sheet with MicrobanÂ® Antimicrobial Features:Color-matched cap, black or off-white substrateThickness ranging from 1.5 mm to 8.9 mmToughness and durabilityEasy to form with good part definitionChemical resistantFire retardantExcellent..
Tensile Strength	42.0 MPa	6090 psi	ASTM D638
KYDEXÂ® XD 3D Laminate Thermoplastic 3D Laminate for Flat Lamination and Membrane Pressed Uses Features:Tough and durableResistant to cracking and chippingSolid, integral color3500+ custom colorsResistant to a wide range of chemicalsAbrasion resistantFire retardantExcellent fabrication qualit..
Tensile Strength	42.0 MPa	6090 psi	ASTM D638
KYDEXÂ® XD MB 3D Laminate Thermoplastic 3D Laminate for Flat Lamination and Membrane Pressed Uses with MicrobanÂ® Features:Tough and extremely durableResistant to cracking and chippingSolid, integral color4,000+ custom colorsResistant to a wide range of chemicalsAbrasion resistantFire retardantVery low moisture..
Tensile Strength	42.0 MPa	6090 psi	ASTM D638
KYDEXÂ® 321 Co-Extruded High Impact Fire Rated Sheet Features:Metallic cap, black, gray or off-white substrateThickness ranging from 3.18 mm to 8.9 mmTextures: P-3 Velour Matte and P-C Level HaircellImpact resistantEasy to form with good part definiti..
Tensile Strength	42.0 MPa	6090 psi	ASTM D638
KYDEXÂ® 331/331d Co-Extruded High Impact Fire Rated Thermoplastic Sheet with Weatherable Acrylic Film Cap KYDEXÂ® 331 is a co-extruded high impact fire rated thermoplastic sheet with a weatherable cap that offers superior performance for thermoforming. It can also be used as an impact resistant surfa..
Tensile Strength	42.0 MPa	6090 psi	ASTM D638
KYDEXÂ® T MB High Impact Fire Rated Thermoforming Sheet with MicrobanÂ® Antimicrobial Product Features:Substitute for FR-ABS sheet with competitive pricing but superior cost/performanceHigher breakage resistanceStandard thicknesses from 0.71 mm to 2.36 mmAmong the most rigid of thermoforming..
Tensile Strength	42.0 MPa	6090 psi	ISO 527-1
Sax Polymers SAXLAC 320 Acrylonitrile Butadiene Styrene Saxalac 320 is a high impact resistant, easy flowing ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% RH.Information provid..
Tensile Strength	42.0 MPa	6090 psi	ISO 527-1
Sax Polymers SAXLAC 320A Acrylonitrile Butadiene Styrene Saxalac 320A is an antistatic, high impact resistant and easy flowing ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% RH.I..
Tensile Strength	42.0 MPa	6090 psi	ISO 527-1
Sax Polymers SAXLAC 320U Acrylonitrile Butadiene Styrene Saxalac 320U is an UV protected, high impact resistant and easy flowing ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tested at 50% RH..
Tensile Strength	42.0 MPa	6090 psi
Corbion Purac Blend B High Heat, High Modulus Homopolymer PLA Heat resistance higher than typical PLA is achieved by addition of a nucleating agent and PDLA homopolymer. Increased modulus is produced by addition of talc to the base grade. Data is for samples..
Tensile Strength	42.0 MPa	6090 psi	cond.; DIN 53 455
Hippe PA 11 Nylon 11 Water armatures, bearing under water, seals, housings, fans, insulated parts, parts for textile machines and household units. Toother wheels, sliding components and guides. Very low water absorpti..
Tensile Strength	>= 42.0 MPa	>= 6090 psi	ISO 37
Austin Novel Materials Texalan® 290A Polyester-based TPU Description: Good abrasion resistance, tensile strength, oil resistance and transparency which can meet different demands in various industryInformation from Dawnentech
Tensile Strength	>= 42.0 MPa	>= 6090 psi	ISO 37
Austin Novel Materials Texalan® 490A Polyester-based TPU Description: Can be considered as custom-made products which use different raw materials to meet customers special requirementsInformation from Dawnentech
Tensile Strength	>= 42.0 MPa	>= 6090 psi	ISO 37
Austin Novel Materials Texalan® 495A Polyester-based TPU Description: Can be considered as custom-made products which use different raw materials to meet customers special requirementsInformation from Dawnentech
Tensile Strength	>= 42.0 MPa	>= 6090 psi	ISO 37
Austin Novel Materials Texalan® 690A Polyester and Polyether based TPU Description: A kind of custom-made products which use different raw materials to meet customers special requirementsInformation from Dawnentech
Tensile Strength	42.0 MPa @Strain 10.0 %, Temperature 60.0 °C	6090 psi @Strain 10.0 %, Temperature 140 °F	50 mm/min; ISO 527-2
BASF Elastollan R 2000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength	42.0 MPa @Strain 20.0 %, Temperature 60.0 °C	6090 psi @Strain 20.0 %, Temperature 140 °F	50 mm/min; ISO 527-2
BASF Elastollan R 2000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength	>= 42.0 MPa	>= 6090 psi	ISO 37
Austin Novel Materials Texalan® 395A Polyester-based TPU Description: Good abrasion resistance, tensile strength, oil resistance which can be used in injection, extrusion purpose.Information from Dawnentech
Tensile Strength	42.0 MPa	6090 psi	ASTM D412
Wanhua Chemical Wanthane® WHT-1164 Polyester Based TPU Excellent mechanical properties, high abrasion resistance, tear resistance, short cycle timeInformation provided by Wanhua Chemical Group Co., Ltd.
Tensile Strength	42.0 MPa	6090 psi	ASTM D412
Wanhua Chemical Wanthane® WHT-1695AB Polyester Based TPU Stable melt viscosity, outstanding toughness & tear resistance, good workability for high frequency weldingInformation provided by Wanhua Chemical Group Co., Ltd.