Polymer Property : Tensile Strength = 5370 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	37.0 MPa	5370 psi	ISO 527
Premix Premi-Glas® 1268 Fiberglass Reinforced Thermoset Thick Molding Compound Premi-Glas® 1268 is a fiberglass reinforced thermoset thick molding compound for composite power train applications such as valve covers and timing gear covers.Key features and benefits are:Ideal f..
Tensile Strength	37.0 MPa @Temperature 23.0 °C	5370 psi @Temperature 73.4 °F	ASTM D638
DuPont Performance Polymers Crastin® ST820 BK503 PBT (Unverified Data**) Crastin® ST820 BK503 is an unreinforced, Super Tough, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength	37.0 MPa	5370 psi	ASTM D412
GRECO ISOTHANE 5080A PolyetherÂ TPUÂ Resin ISOTHANE 5000 Series products are polyether based thermoplastic polyurethanes. They exhibit excellent bio-compatibility, hydrolytic resistance, fungus resistance, and low temperature performance pro..
Tensile Strength	37.0 MPa	5370 psi	Weld; ASTM D638
Kuraray Genestarâ„¢ GA2330 Nylon, 33% Glass Filled Abrasion Resistance V-0 Grade. Can be used for applications requiring high abrasion and heat resistance, as well as flame retardancy, such as internal gear of copying machine.
Tensile Strength	37.0 MPa	5370 psi
Lucite International LuciteÂ® 30B Acrylic Resin for Dental Applications Lucite 30B is a designed for use in the manufacture of dental appliances. Lucite 30B resin contains residual initiator which allows this polymer to be processed using either dough molding or dry com..
Tensile Strength	37.0 MPa	5370 psi	ASTM D412
GRECO ISOTHANE 2080A Poly(caprolactone)ester TPUÂ Resin ISOTHANE 2000 series products are polyester poly(caprolactone)ester based thermoplastic polyurethane. They exhibit excellent toughness, abrasive resistance, solvent resistance, and hydrolysis stabi..
Tensile Strength	37.0 MPa	5370 psi	ASTM D412
GRECO ISOTHANE 3085A PolyetherÂ TPUÂ Resin ISOTHANE 3000 Series products are polyether based thermoplastic polyurethanes. They exhibit excellent hydrolytic resistance, fungus resistance, and low temperature performance properties. These prod..
Tensile Strength	37.0 MPa	5370 psi	5 mm/min; ISO 527-1
Sax Polymers SAXALEN PPH335T20 Polypropylene Homopolymer, 20% Talc Filled SAXALEN PPH335T20 is a 20% mineral filled Polypropylene - Homopolymer intended for injection molding with very good flow properties and higher stiffness by low warpage and good surface appearance.In..
Tensile Strength	37.0 MPa	5370 psi	ISO 527-1
Sax Polymers SAXATEC 6120 AES SAXATEC 6120 is a easy lowing, weatherable AES injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion.Information provided by SAX Polym..
Tensile Strength	37.0 MPa	5370 psi	ASTM D412
Wanhua Chemical Wanthane® WHT-1490IV Polyester Based TPU Good extrusion stability, high transparency, excellent mechanical propertiesInformation provided by Wanhua Chemical Group Co., Ltd.
Tensile Strength	37.0 MPa	5370 psi	DIN EN ISO 527
Wolf Kunststoff ZEDEX® ZX-100EL55 A1F Polymer Alloy, Elastomer Modified Main Characteristics: Rubbery; Soft; High shock absorption; High impact resistance; Elongation > 300%Applications: Handling, Vessel and Pump, Steel and Water, Chemical Engineering, Automitve Technol..
Tensile Strength	37.0 MPa	5370 psi	ASTM D412
Wanhua Chemical Wanthane® WHT-1690AB Polyester Based TPU Stable melt viscosity, outstanding toughness & tear resistance, good workability for high frequency weldingInformation provided by Wanhua Chemical Group Co., Ltd.
Tensile Strength	37.0 MPa	5370 psi	ISO 527
Lucite International Elvakon® 4451 Super Low Gloss Acrylic Capstock Coextrusion grade developed to provide high aesthetic control, outstanding weatherability and impact and scratch resistance, the Elvakon® series enables protection of substrates with a durable prot..