Polymer Property : Tensile Strength = 41.4 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	>= 41.4 MPa	>= 6000 psi	ASTM D638
S&E Specialty Polymers GR-1409 PVC Application: High flow, high impact rigid PVC based compound. It is suitable for injection molding of the large parts.Information provided by S&E Specialty Polymers
Tensile Strength	41.4 MPa	6000 psi	ASTM D412
Northstar Polymers MSS-A80AQ High Performance Polyurethane Cast Elastomer System 80A This is a Ester/MDI base high-performance polyurethane casting system. This systems is recommended to applications in which the part requires high tensile strength, cut/tear resistance, dry-abrasio..
Tensile Strength	41.4 MPa	6000 psi	Substrate Property; ASTM D412
Arlon R36798T017 0.017" (0.432 mm) Uncured Silicone Rubber with Laminated Tefzel® Substrate (discontinue Design/Construction: Liner: PTFE Coated Fiberglass Side 1: Uncured Silicone Rubber Substrate: Laminated Tefzel® Substrate: Treated for adhesionAppearance: Translucent, high viscosity gum on fluoro..
Tensile Strength	41.4 - 51.7 MPa	6000 - 7500 psi	ASTM D638
Mar-Bal MB2000-15 Thermoset Polyester Composite Molding Compound An excellent flame and track resistant material with excellent electrical and mechanical properties. Good dielectric strength and low shrink for close dimensional control.Mar-Bal standard grades can..
Tensile Strength	41.4 - 62.1 MPa	6000 - 9000 psi	ASTM D638
Mar-Bal MB3000-20NY Thermoset Polyester Composite Molding Compound A superior chemical resistant material with excellent flame and track resistance.Mar-Bal standard grades can be injection, compression and transfer molded.Information provided by Mar-Bal, Inc.
Tensile Strength	41.4 - 55.2 MPa	6000 - 8000 psi	ASTM D638
Mar-Bal MB5500 Thermoset Polyester Composite Molding Compound A superior heat resistant material. U.L. RTI rating of 160Â°C-170Â°C.Mar-Bal standard grades can be injection, compression and transfer molded.Information provided by Mar-Bal, Inc.
Tensile Strength	41.4 MPa	6000 psi	ASTM D638
Techmer ES HiFill FRÂ® PBT/ABS FR Availability: North AmericaForms: PelletsFeatures: Flame RetardantProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
Tensile Strength	41.4 MPa	6000 psi	ASTM D638
Techmer ES LuriblendÂ® POM CO TS20 Acetal Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(20%) and Silicone LubricantFeatures: Lubricated, Good Wear Resistance and CopolymerInformation provided by TP Composites, Inc.
Tensile Strength	41.4 MPa	6000 psi	ASTM D412
Teknor Apex LaripurÂ® LPR 7560EG Thermoplastic Polyurethane Features: - Excellent performance under extreme and aggressive environments - Superior abrasion and cut resistance - Resistance to chemical, microbial attack and hydrolysis - Excellent flexibility a..
Tensile Strength	41.4 MPa	6000 psi	ASTM D638
Techmer ES ElastoblendÂ® PA6/ABS 1120 B1 Availability: North AmericaForms: PelletsAdditive: Impact ModifierFeatures: Impact ModifiedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
Tensile Strength	41.4 MPa @Temperature 23.9 °C	6000 psi @Temperature 75.0 °F
Master Bond MB306 Low Viscosity Methyl Cyanoacrylate Features superior bonding properties. Master Bond MB306 is a single component, low viscosity, rapid setting, methyl cyanoacrylate adhesive. Similar to other types of “super glue”, MB306 cures ver..
Tensile Strength	41.4 MPa	6000 psi	ASTM D412
Lubrizol ESTANE® 58630 Ether Based Thermoplastic Polyurethane Features: Good physical properties, hydrolysis resistance, low temperature performance and abrasion along with wide processing window for extrusion and low surface tack.Uses: Blown and flat die/cast..
Tensile Strength	41.4 MPa	6000 psi	ASTM D638
Ecomass® 1700CO94 Copper Powder Filled Polyamide, Injection Molding High Specific Gravity, Copper Powder Filled Polyamide (PA), Rigid, Product Form - PelletsProcessing Method: Injection MoldingNontoxic alternative to Lead, weighting and balancing applicationsInform..
Tensile Strength	41.4 MPa	6000 psi	2 in/min; ASTM D638
Braskem F350HC2 High Crystallinity Homopolymer Polypropylene Description: Very High Flexural ModulusApplications: Suggested Uses Include Compounding, Automotive, AppliancesThis resin meets the requirements for olefin polymers as defined in 21 CFR, section 177..
Tensile Strength	41.4 MPa	6000 psi	Laminated ETFE Film Property; Arlon SQA-TMS-008
Arlon 25188T020 0.020" Uncured Silicone Rubber/Laminated ETFE Film Design/Construction:Liner: 0.003" PTFE Coated FiberglassSide 1: Uncured Silicone RubberSubstrate: Laminated ETFE Film-treated for adhesionThis data represents typical values for the production ma..
Tensile Strength	41.4 MPa	6000 psi	Laminated ETFE Film; ASTM D638
Arlon 25662T010 0.010" (0.254 mm) Cured Silicone Rubber with Laminated ETFE Film Substrate Design/Construction:Side 1: Cured Silicone RubberSubstrate: Laminated ETFE FilmChemical Compatibility: (ETFE offers good chemical resistance to the following classes of chemicals) Alkalis, Organic a..
Tensile Strength	41.4 MPa	6000 psi	Substrate Property; ASTM D412
Arlon R37208T017 0.017" (0.432 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Liner Design/Construction: Liner: PTFE Coated Fiberglass Side 1: Uncured Silicone Rubber Substrate: Laminated Tefzel® Substrate: Treated for adhesionThis data represents typical values for the productio..
Tensile Strength	41.4 MPa	6000 psi	ASTM D638
Americas Styrenics MC3700 High Heat Crystal Polystyrene Product CharacteristicsEasy filling of thin-walled partsExceptional mold releaseImproved cycle times in hard to fill partsFood Contact CompliantUL Classification 94HBUSP Class VITypical Applications..
Tensile Strength	41.4 MPa	6000 psi	Laminated ETFE Film Property; ASTM D638
Arlon R36812T010 0.010" Cured Silicone Rubber with Laminated ETFE Film Substrate Design/Construction:Liner: N/ASide 1: Cured Silicone RubberSubstrate: Laminated ETFE FilmChemical Compatibility: Alkalis, Organic and Inorganic acids, Amines, Epoxies, Aromatic compounds, Chlorin..