Polymer Property : Tensile Strength = 11300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength	78.0 MPa	11300 psi	at Yield; ISO 527-1/-2
Quadrant EPP Ertacetal® H POM-H, extruded (ISO Data) Ertacetal H is Quadrant’s homopolymer acetal grade. It offers a higher mechanical strength, stiffness, hardness and creep resistance as well as a lower thermal expansion rate and often also a bette..
Tensile Strength	78.0 MPa	11300 psi	at Break (NYP); ISO 527-1/-2
Quadrant EPP Ketron® HPV PEEK + carbon fibres + PTFE + graphite, bearing grade, extruded (ISO Data) The addition of carbon fibres, PTFE and graphite to virgin PEEK results in a Ketron PEEK “bearing grade”. Its excellent tribological properties (low friction, long wear and high pressure-velocity ..
Tensile Strength	78.0 MPa	11300 psi	at Break (NYP); ISO 527-1/-2
Quadrant EPP Techtron® HPV PPS + solid lubricant, bearing grade, extruded (ISO Data) As a reinforced, internally lubricated PPS grade, Techtron HPV PPS demonstrates an excellent combination of properties including wear resistance, load-bearing capabilities and dimensional stability ..
Tensile Strength	77.9 MPa	11300 psi	ASTM D638
Solvay Specialty Polymers Udel® GF-110 Polysulfone (PSU) (Unverified Data**) Udel GF-110, resin is a 10% glass fiber reinforced polysulfone (PSU). Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resista..
Tensile Strength	77.9 MPa	11300 psi	ASTM D638
Solvay Specialty Polymers UdelÂ® GF-110 Polysulfone (PSU), Glass Fiber UdelÂ® GF-110, resin is a 10% glass fiber reinforced polysulfone (PSU). Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical res..
Tensile Strength	78.0 MPa	11300 psi	50 mm/min; ISO 527-1
Sax Polymers SAXAMID 126K6 Nylon 6, 30% Glass Filled SAXAMID 126K6 is a 30% glass beads filled polyamide 6 injection-molding-grade. It is characterized by dimensional stability, low warpage and good surface quality.Information provided by SAX Polymers..
Tensile Strength	78.0 MPa	11300 psi	DIN EN ISO 527
Wolf Kunststoff ZEDEX® ZX-100K A1K Polymer Alloy Main Characteristics: Hard; Stiff; Tough; High fatigue strength; Good weather resistance; Good machinability; FDA compliant LABS; PTFE and silicone-free; KTW approved; Stress resistantApplications: ..
Tensile Strength	78.0 MPa	11300 psi	cond.; ISO 527
Azoty Tarnow™ Tarnamid® T-27 GF10 MX10 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grade, reinforced with 10% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning, good surface quality.T..
Tensile Strength	78.0 MPa @Strain 12.0 %, Temperature 23.0 °C	11300 psi @Strain 12.0 %, Temperature 73.4 °F	50 mm/min; ISO 527-2
BASF Elastollan R 3000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength	78.0 MPa @Strain 8.00 %, Temperature 23.0 °C	11300 psi @Strain 8.00 %, Temperature 73.4 °F	50 mm/min; ISO 527-2
BASF Elastollan R 3000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength	78.0 MPa	11300 psi	5 mm/min; ISO 527-1
Sax Polymers SAXALEN PPH304G25 Polypropylene Homopolymer, 25% Glass Filled SAXALEN PPH304G25 is a 25% glass filled Polypropylene - Homopolymer intended for injection molding. This compound is characterized by high stiffness good impact resistance und reduced creep under lo..
Tensile Strength	77.9 - 91.7 MPa	11300 - 13300 psi
Bulk Molding Compounds BMC T45HT Automotive Grade Molding compound BMC T45HT was designed for the very demanding applications of automotive under hood engine covers. It meets the GMP UP .007 specification for automotive under hood. BMC T45HT is a vinyl ester base..