Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 7.58 MPa | 1100 psi | ASTM D638 |
Quadrant EPP Fluorosint® 500 PTFE, synthetic mica-filled PTFE, compression molded (ASTM Product Data Sheet) |
|||
Tensile Strength | 7.58 MPa @Strain 100 % |
1100 psi @Strain 100 % |
510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 86479 Natural Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength | 7.58 MPa @Strain 100 % |
1100 psi @Strain 100 % |
510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 86479 Tran Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Typical |
Garlock 2264 C.I. EPDM Sheet Rubber, Polyester Insert Garlock cloth-inserted materials are designed to add stability where mechanical fastening is necessary, and to reduce gasket creep where heavy flange loading is required.Style #2564 is a smooth fini.. |
|||
Tensile Strength | 7.60 MPa | 1100 psi | Flatwise |
Henkel Hysol EA 9628H Film Adhesive First generation, modified epoxy film, high peel strength, good stress, environmental resistance and structural propertiesApplications: Composite Bonding, Metal & Honeycomb BondingData from .060 psf.. |
|||
Tensile Strength | 7.60 MPa | 1100 psi | |
Henkel SynSpand EA 9890 Expanding Syntactic Film Expanding modified epoxy film, cures at 250°F / 121°C, used for jet engine abradable fan seals. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon 30300R062 0.062" (1.57 mm) Uncured Silicone Rubber on Kodacel Carrier Design/Construction: Interleave: Polyethylene Side 1: Uncured Silicone RubberCarrier: KodacelAppearance: Red silicone gum on polymer linersThis data represents typical values for the production mate.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon 41300R062 0.062" Uncured Silicone Rubber on Holland Cloth Design/Construction:Interleave: 3.0 mil PolyethyleneSide 1: Uncured Silicone RubberCarrier: Holland ClothThis data represents typical values for the production material and should not be used as m.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Side 2, Silicone Property; ASTM D412 |
Arlon 51576B015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone RubberSubstrate: 7628 Style Fiberglass Side 2: Uncured Silicone RubberInterleave: Polyethylene This data represents typical values for the production mate.. |
|||
Tensile Strength | 7.60 MPa | 1100 psi | 100; ISO 37 |
BASF Elastollan 1085 A TPUR Description: Thermoplastic Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tear and tensile strength, good damping characteristics and a high resilien.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon 55572R030 0.030" (0.762 mm) Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSubstrate: Style 162 Fiberglass Appearance: Red silicone rubber on fiberglass clothThis data Represents typical values for the production material. T.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon 55572XA028 0.028" (0.711 mm) Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSubstrate: Style 162 Fiberglass This data Represents typical values for the production material. The data should not be used to write, or in place of.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Side 2 Silicone Property; ASTM D412 |
Arlon 55576R060 0.060" Cured/Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSubstrate: Style 162 FiberglassSide 2: Uncured Silicone RubberInterleave: 3 mil PEThis data represents typical values for the production material .. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Side 1, Layer 2; Compound Property; ASTM D412 |
Arlon 55578R030 0.0325" (0.825 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Interleave: PolyethyleneSide 1, Layer 2: Uncured Silicone Rubber Side 1, Layer 1: Cured Silicone Rubber Substrate: Style 162 Fiberglass Side 2: Cured Silicone Rubber Appearance:.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Side 2, Layer 2; Compound Property; ASTM D412 |
Arlon 55578R036 0.036" (0.914 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Interleave: PolyethyleneSide 2, Layer 2: Uncured Silicone Rubber Side 2, Layer 1: Cured Silicone Rubber Substrate: Style 162 Fiberglass Side 1: Cured Silicone Rubber Appearance:.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon 55578XA028 0.0280" Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: LDPESide 2 Layer 2: Uncured Silicone RubberSide 2 Layer 1: Cured Silicone RubberSubstrate: Style 162 FiberglassSide 1: Cured Silicone RubberThis data represents ty.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon 55579XA028 0.0295" Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: LDPELayer 2: Uncured Silicone RubberLayer 1: Cured Silicone RubberSubstrate: Style 162 FiberglassThis data represents typical values for the production material an.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Layer 2 Silicone Property; ASTM D412 |
Arlon 56579R028 0.0295" Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: 2.5 mil PELayer 2: Uncured Silicone RubberLayer 1: Cured Silicone RubberSubstrate: Style 1564 FiberglassThis data represents typical values for the production mate.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon 99570R010 0.010" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier Design/Construction:Liner: 0.001" FEP FilmSide 1: Uncured Silicone RubberCarrier: 0.003" PTFE coated FiberglassThis data represents typical values for the production material and should not be us.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon LW201B##-P0 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) Description: 1 inch wide, 20 mil thick, Black, Triangular cross-section, Self-Fusing Silicone Tape. Product is supplied in various roll lengths and the ## in the product number indicates roll length.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon LW201B##-P1 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) Description: 1 inch wide, 20 mil thick, Black, Triangular cross-section, Self-Fusing Silicone Tape. Product is supplied in various roll lengths and the ## in the product number indicates roll length.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon LW5015Y##-M1 0.050" (1.27 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported) Description: 1.5 inch wide, 50 mil thick, Yellow, Triangular cross-section, Self-Fusing Silicone Tape. Product is supplied in various roll lengths and the ## in the product number indicates roll len.. |
|||
Tensile Strength | >= 7.58 MPa | >= 1100 psi | Compound Property |
Arlon R34172W008 0.008" (0.203 mm) Cured, Unsupported Silicone Rubber on a Mylar Carrier Design/Construction:Side 1: Cured, Unsupported Silicone Rubber on a Mylar Carrier This data Represents typical values for the production material. The data should not be used to write, or in place o.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | |
AlphaGary AlphaSeal™ 07-193-C Natural Thermoplastic Elastomer AlphaSeal™ 07-193-C Natural is recommended for the skin over extruded foamed corks. AlphaSeal is formulated for low taste and low odor and exhibits good elastic recovery, abrasion resistance and l.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Side 2, Silicone Property; ASTM D412 |
Arlon 51576R031 0.031" (0.787 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Interleave: Polyethylene Side 1: Cured Silicone RubberSubstrate: 7628 Style Fiberglass Side 2: Uncured Silicone Rubber This data represents typical values for the production mat.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Side 2, Silicone Property; ASTM D412 |
Arlon 51576W015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone RubberSubstrate: 7628 Style Fiberglass Side 2: Uncured Silicone Rubber Interleave: Polyethylene Appearance: White silicone gum on glass fabricThis data re.. |
|||
Tensile Strength | >= 7.58 MPa | >= 1100 psi | Silicone Property |
Arlon 55503R062 0.062" Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: 3 mil PolyethyleneSide 1: Cured Silicone RubberSubstrate: Prime Coated 162 Style FiberglassSide 2: Cured Silicone RubberThis data represents typical values for th.. |
|||
Tensile Strength | 7.60 MPa | 1100 psi | |
Momentive Performance Materials TSE 2287 Heat Cured Rubber - High Duro Translucent Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 |
Arlon 32300R062 0.062" (1.57 mm) Uncured Silicone Rubber on PET Carrier Design/Construction: Interleave: PolyethyleneSide 1: Uncured Silicone RubberCarrier: PETAppearance: Red silicone gum on polymer release linerThis data represents typical values for the production ma.. |
|||
Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; Arlon SQA-TMS-008 |
Arlon 32570XA020 0.020" Uncured Silicone Rubber on Polyester Film Carrier Design/Construction:Interleave: 0.0025" PolyethyleneSide 1: Uncured Silicone RubberCarrier: Polyester FilmThis data represents typical values for the production material and should not be used as .. |