Polymer Property : Tensile Strength = 10000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength 68.9 MPa
10000 psi
ASTM D-638
Plaskolite West Optix® CP - 80 General Purpose Acrylic Resin
Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av..
Tensile Strength 68.9 MPa
10000 psi
ASTM D638
Quadrant EPP Nylatron® GSM Blue Nylon, Cast Oil & MoS2 Filled Type 6 (ASTM Product Data Sheet)
Tensile Strength 68.9 MPa
10000 psi
ASTM D638
Ravago Manufacturing Americas Hylex® P1025L Polycarbonate, High Flow, Mold Release
Information provided by Ravago
Tensile Strength 68.9 MPa
10000 psi
ASTM D638
Quadrant EPP Duratron® PAI T4501 Polyamide-imide, compression molded bearing grade (ASTM Product Data Sheet)
Tensile Strength 68.9 MPa
10000 psi
ASTM D638
Quadrant EPP Semitron® 420 ESd V (ASTM Product Data Sheet)
Tensile Strength 68.9 MPa
10000 psi
ASTM D638
Quantum Polycarbonate
Information provided by Quantum Advanced Engineering Plastics
Tensile Strength 68.9 MPa
10000 psi
ASTM D638
Haysite H722 Polyester, Glass Reinforced
H722 is an all-purpose GPO-1 fiberglass mat reinforced thermoset polyester molded sheet. Available in thicknesses ranging from .031" - 2.00". Standard color - Natural. Meets Gov't Specs - LP-509, ..
Tensile Strength 68.9 MPa
10000 psi
Specialty Coating Systems Parylene C Poly (P-Xylylene) Coating
Parylene C is a polymer of para-xylylene modified by the substitution of a chlorine atom for one of the aromatic hydrogen atoms. Parylene C has a useful combination of electrical and physical proper..
Tensile Strength >= 68.9 MPa
>= 10000 psi
Master Bond Ep46HT-2 Two Component, Heat Resistant Epoxy System
Master Bond Polymer System EP46HT-2 is a two component epoxy system for bonding, sealing and casting applications where resistance to temperatures from -100°F to +500°F is required. It is 100% rea..
Tensile Strength >= 68.9 MPa
>= 10000 psi
Master Bond EP46HT-2Med Two Component Heat Resistant Biocompatible Epoxy System
Master Bond Polymer System EP46HT-2MED is a two component medical grade epoxy system for high performance structural bonding and casting suitable for applications where resistance to temperatures fr..
Tensile Strength >= 68.9 MPa
>= 10000 psi
Master Bond EP41SMed Two Component, Low Viscosity, USP Class VI Epoxy System
Master Bond Polymer Adhesive EP41S Medical is a two component low viscosity epoxy resin system for high performance bonding, sealing, coating, as well as small encapsulations, pottings and castings...
Tensile Strength 68.9 MPa
10000 psi
in plane
Carlisle 201LL Carbon-Carbon Composite
Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t..
Tensile Strength 68.9 MPa
10000 psi
Cross; IPC TM-650 2.4.18.3
Arlon MULTICLAD™ HF Halogen-Free Low-Loss Laminate and Prepreg System
MULTICLAD™ HF represents the next generation low-loss thermoset and prepreg system for high-speed and high-frequency printed circuit boards. This technology combines a low-loss, high reliability t..
Tensile Strength 68.9 MPa
10000 psi
in plane
Carlisle 201HL Carbon-Carbon Composite
Carbon-Carbon Composite manufactured as sheets from 4mm to 125mm thick this material is essentially a fracture tough, fiber reinforced graphite often referred to as a “CFC”. Good for use in air t..
Tensile Strength 69.0 MPa

@Strain 10.0 %,
Temperature 23.0 °C
10000 psi

@Strain 10.0 %,
Temperature 73.4 °F
50 mm/min; ISO 527-2
BASF Elastollan R 2000 20% Glass Filled TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength 69.0 MPa

@Strain 20.0 %,
Temperature 23.0 °C
10000 psi

@Strain 20.0 %,
Temperature 73.4 °F
50 mm/min; ISO 527-2
BASF Elastollan R 2000 20% Glass Filled TPUR
Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan..
Tensile Strength 68.9 MPa
10000 psi
ASTM D-638
Plaskolite Optix® CP - 80 General Purpose Acrylic Resin
OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli..
Tensile Strength 68.9 MPa
10000 psi
ASTM D638
Quantum Acetal-Homopolymer
Information provided by Quantum Advanced Engineering Plastics
Tensile Strength 68.9 - 82.7 MPa
10000 - 12000 psi
Bulk Molding Compounds BMC T40(20) Die Casting Replacement Grade Molding Compound
BMC T40(20) was formulated as a direct replacement for aluminum die casting applications. T40(20) is UL recognized. Excellent mechanical properties and dimensional control allow molded parts to ma..
Tensile Strength 68.9 - 82.7 MPa
10000 - 12000 psi
Bulk Molding Compounds BMC T40-4020-AQ High Strength Arc Quenching Molding Compound
BMC T40-4020-AQ was formulated as a high strength arc quenching material for electrical applications. Typical applications are arc hoods and electrical contactors.Information provided by Bulk Moldi..