Polymer Property : Linear Mold Shrinkage, Flow = 0.027 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.027 - 0.030 cm/cm

@Time 86400 sec
0.027 - 0.030 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP STAT-KON FX98500 PE
LNP* STAT-KON* FX98500 is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Linear Mold Shrinkage, Flow 0.027 - 0.030 cm/cm

@Time 86400 sec
0.027 - 0.030 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP STAT-KON FX98500 PE
LNP* STAT-KON* FX98500 is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Linear Mold Shrinkage, Flow 0.027 - 0.030 cm/cm

@Time 86400 sec
0.027 - 0.030 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer
LNP THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing 20% Milled Glass.
Linear Mold Shrinkage, Flow 0.027 - 0.030 cm/cm

@Time 86400 sec
0.027 - 0.030 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer
LNP THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing 20% Milled Glass.
Linear Mold Shrinkage, Flow 0.027 - 0.030 cm/cm

@Time 86400 sec
0.027 - 0.030 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer (Asia Pacific)
LNP* THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass.
Linear Mold Shrinkage, Flow 0.027 - 0.030 cm/cm

@Time 86400 sec
0.027 - 0.030 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP THERMOCOMP KZ004 Acetal Copolymer (Asia Pacific)
LNP* THERMOCOMP* KZ004 is a compound based on Acetal Copolymer resin containing Glass Fiber, Milled Glass.
Linear Mold Shrinkage, Flow 0.027 - 0.030 cm/cm

@Time 86400 sec
0.027 - 0.030 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP STAT-KON FX98500C PE
LNP* STAT-KON* FX98500C is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Linear Mold Shrinkage, Flow 0.027 - 0.030 cm/cm

@Time 86400 sec
0.027 - 0.030 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP STAT-KON FX98500C PE
LNP* STAT-KON* FX98500C is a compound based on Polyethylene resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Linear Mold Shrinkage, Flow 0.027 cm/cm

@Time 86400 sec
0.027 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP STAT-KON RD000 PA 66
LNP STAT-KON* RD000 is a compound based on Nylon 66 resin containing Carbon Powder. Added feature of this material is: Electrically Conductive.