Polymer Property : Linear Mold Shrinkage, Flow = 0.013 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK LNP* LUBRICOMP* LL004C is a compound based on Polyetheretherketone resin containing 20% PTFE. Added features of this material include: Wear Resistant, Clean Compounding System.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK LNP* LUBRICOMP* LL004C is a compound based on Polyetheretherketone resin containing 20% PTFE. Added features of this material include: Wear Resistant, Clean Compounding System.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK (Asia Pacific) LNP* Lubricomp* LL004C is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated, Clean Compounding System.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK (Asia Pacific) LNP* Lubricomp* LL004C is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated, Clean Compounding System.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK LNP* LUBRICOMP* LL004E is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK LNP* LUBRICOMP* LL004E is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK (Asia Pacific) LNP* Lubricomp* LL004E is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK (Asia Pacific) LNP* Lubricomp* LL004E is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 LNP* LUBRICOMP* RFL34 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 LNP* LUBRICOMP* RFL34 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 (Asia Pacific) LNP* Lubricomp* RFL34 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.013 - 0.016 cm/cm @Time 86400 sec	0.013 - 0.016 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON MD000 PP LNP STAT-KON* MD000 is a compound based on Polypropylene resin containing Carbon Powder. Added feature of this material is: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.013 - 0.016 cm/cm @Time 86400 sec	0.013 - 0.016 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON MD000 PP (Asia Pacific) LNP STAT-KON* MD000 is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp WFB51 PBT LNP THERMOCOMP* WFB51 is a compound based on Polybutylene Terephalate resin containing Glass Bead, Glass Fiber. Added features of this material include: Low Warpage.This data was supplied by SABIC-..
Linear Mold Shrinkage, Flow	0.013 - 0.015 cm/cm @Time 86400 sec	0.013 - 0.015 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact.
Linear Mold Shrinkage, Flow	0.013 - 0.015 cm/cm @Time 86400 sec	0.013 - 0.015 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK (Asia Pacific) LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK (Asia Pacific) LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK (Europe-Africa-Middle East) LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK (Europe-Africa-Middle East) LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP MB008S PP LNP* THERMOCOMP* MB008S is a compound based on Polypropylene resin containing 40% Glass Bead. Added features of this material include: Heat Stabilized.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP Thermocomp MB008S PP (Asia Pacific) LNP* Thermocomp* MB008S is a compound based on Polypropylene resin containing Glass Bead. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pa..
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WX02869H Polyester, TP LNP THERMOCOMP* WX02869H is a compound based on Polyester, TP resin containing High Specific Gravity. Added features of this material include: High Impact.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP WX02869H Polyester, TP LNP THERMOCOMP* WX02869H is a compound based on Polyester, TP resin containing High Specific Gravity. Added features of this material include: High Impact.
Linear Mold Shrinkage, Flow	0.013 - 0.015 cm/cm @Time 86400 sec	0.013 - 0.015 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 (Asia Pacific) LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact.
Linear Mold Shrinkage, Flow	0.013 - 0.015 cm/cm @Time 86400 sec	0.013 - 0.015 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOTUF V1000 PA 66 (Asia Pacific) LNP THERMOTUF* V1000 is a compound based on Nylon resin. Added features of this material include: High Impact.
Linear Mold Shrinkage, Flow	0.013 cm/cm @Thickness 2.00 mm	0.013 in/in @Thickness 0.0787 in	DAM; ISO 294-4
DuPont Performance Polymers Zytel® SC315 NC010 Nylon 612 (Unverified Data**) Zytel® SC315 NC010 is an unreinforced, lubricated 612 polyamide suitable for injection molding. It has been developed for applications such as parts for the healthcare industry.Information provided..
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP STAT-KON MS000IL PP LNP* STAT-KON* MS000IL is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: High Impact, Low Extractible, Electrically Conductive, food c..