Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Cycoloy® XCY620HS PC+ABS PC+ ABS General Purpose Non-FR |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Cycoloy® XCY620S PC+ABS PC+ ABS Automotive applications |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Cycoloy® XCY620S PC+ABS (Europe-Africa-Middle East) PC+ ABS automotive applications, excellent flow/impact balance, high heat resistance temperature and excellent properties retention after hydrolytic and heat aging. |
|||
Melt Index of Compound | 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Lexan® ML3732 PC (Europe-Africa-Middle East) Lexan ML3732 is a low viscosity flame retardant grade, especially designed to pass the glow wire test according EDF HN60-S-02 at a thickness of 3.2 mm. |
|||
Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 280 °C |
20 g/10 min @Load 4.76 lb, Temperature 536 °F |
|
Honeywell Aegis™ OX High Barrier Nylon
(discontinued **) Description: Aegis OX is an oxygen-scavenging nylon. Oxygen barrier is comparable to a glass bottle with metal crown closure. In addition Aegis OX provides CO2 barrier and possesses glass-like cla.. |
|||
Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
20 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® 325FC PBT (Europe-Africa-Middle East) Commercial, VALOX 325FC is compliant with food contact regulations. VALOX 325FC is a general purpose, unreinforced PBT injection moulding resin which contains internal mold release. This new 325FC g.. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 250 °C |
20 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® 553 PBT (Europe-Africa-Middle East) VALOX 553 is a 30% glass fibre reinforced, flame retardant PBT+PC blend with good warpage characteristics. Applications: appliance handles, spotlights, electric motors, pumphousings. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 250 °C |
20 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® 8032UX PBT+PET (Europe-Africa-Middle East) VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housin.. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 265 °C |
20 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® ENH4550 PBT (Asia Pacific) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 250 °C |
20 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 265 °C |
20 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® ENH4565 PBT (Asia Pacific) 33% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin, Good thermal shock resistance and low CTE. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 265 °C |
20 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® ENH4565 PBT (Europe-Africa-Middle East) 33% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin, Good thermal shock resistance and low CTE. |
|||
Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 265 °C |
20 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 265 °C |
20 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Asia Pacific) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 265 °C |
20 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 300 °C |
20 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics NORYL LTA6020 PPE+PS (Asia Pacific) |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 265 °C |
20 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® EXVX1403 PBT (Asia Pacific) 33% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin, Good thermal shock resistance and low CTE. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 265 °C |
20 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® IQNH4565 PBT (Asia Pacific) Valox* iQNH4565 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 29% based on EPEAT.. |
|||
Melt Index of Compound | 20 g/10 min @Load 1.20 kg, Temperature 280 °C |
20 g/10 min @Load 2.65 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics NORYL FP3060 PPE+PS (Europe-Africa-Middle East) Noryl* FP3060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR .. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 300 °C |
20 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics NORYL LTA6020 PPE+PS (Europe-Africa-Middle East) |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 230 °C |
20 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade DescriptionFormion® FI 131E is an adhesive grade extrusion product. It has been formulated to provide adhesion as a tie layer or resin modifier to bond Ionomer to polar and non polar substances, s.. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 230 °C |
20 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade DescriptionFormion® FI 131E is an adhesive grade extrusion product. It has been formulated to provide adhesion as a tie layer or resin modifier to bond Ionomer to polar and non polar substances, s.. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 230 °C |
20 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade DescriptionFormion® FI 131E is an adhesive grade extrusion product. It has been formulated to provide adhesion as a tie layer or resin modifier to bond Ionomer to polar and non polar substances, s.. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 230 °C |
20 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade DescriptionFormion® FI 131E is an adhesive grade extrusion product. It has been formulated to provide adhesion as a tie layer or resin modifier to bond Ionomer to polar and non polar substances, s.. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 230 °C |
20 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade DescriptionFormion® FI 131E is an adhesive grade extrusion product. It has been formulated to provide adhesion as a tie layer or resin modifier to bond Ionomer to polar and non polar substances, s.. |
|||
Melt Index of Compound | 20 g/10 min @Load 5.00 kg, Temperature 230 °C |
20 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
A. Schulman FORMION™ FI 131E Adhesive, Extrusion Grade DescriptionFormion® FI 131E is an adhesive grade extrusion product. It has been formulated to provide adhesion as a tie layer or resin modifier to bond Ionomer to polar and non polar substances, s.. |
|||
Melt Index of Compound | 20 g/10 min @Load 1.20 kg, Temperature 280 °C |
20 g/10 min @Load 2.65 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics NORYL PX2060 PPE+PS (Asia Pacific) Noryl* PX2060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR .. |
|||
Melt Index of Compound | 20 g/10 min @Load 1.20 kg, Temperature 280 °C |
20 g/10 min @Load 2.65 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics NORYL PX2060 PPE+PS (Europe-Africa-Middle East) Noryl* PX2060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR .. |
|||
Melt Index of Compound | 20 g/10 min @Load 1.20 kg, Temperature 280 °C |
20 g/10 min @Load 2.65 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics NORYL PX2060 PPE+PS Noryl* PX2060 is an unfilled, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and high flow , this resin also uses non-chlorinated, non-brominated FR .. |