Polymer Property : High Load Melt Index = 8.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg
8.0 g/10 min

@Load 47.6 lb
ISO 1133
Total Finathene® WR 201 B N HDPE blow molding  (discontinued **)
FINATHENE® WR 201 B N is a high density polyethylene produced by the slurry loop low pressure polymerization process. FINATHENE® WR 201 B N has been developed for the blow molding of Plastic Fuel ..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg,
Temperature 190 °C
8.0 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Ineos TUB 121NTW HDPE
TUB121 NTW is a natural high density bimodal polyethylene copolymer designed for extrusion of large diameter, thick wall piping for potable water, industrial and mining applications. When blended wi..
High Load Melt Index 8.0 - 14 g/10 min

@Load 21.6 kg,
Temperature 190 °C
8.0 - 14 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238-00
Ipiranga Petrochem GM 5010 T2 HDPE
IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
High Load Melt Index 8.0 - 14 g/10 min

@Load 21.6 kg,
Temperature 190 °C
8.0 - 14 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238-00
Ipiranga Petrochem GM 9245 F HDPE
IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
High Load Melt Index 8.0 - 14 g/10 min

@Load 21.6 kg,
Temperature 190 °C
8.0 - 14 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238-00
Ipiranga Petrochem GM 7040 G HDPE
IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg,
Temperature 190 °C
8.0 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133 cond. 7
Total 49080 UV HDPE blow molding
FINATHENE® 49080 UV is produced by the slurry loop low pressure polymerization process. FINATHENE® 49080 UV is a U.V.-stabilized, high molecular weight pelletized resin, intended for the productio..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg
8.0 g/10 min

@Load 47.6 lb
ISO 1133
Total MS 201 B HDPE blow molding
FINATHENE® MS 201 B is a high density polyethylene produced by a low pressure slurry polymerization process. FINATHENE® MS 201 B has been developed for the blow molding of Plastic Fuel Tanks and a..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg
8.0 g/10 min

@Load 47.6 lb
ISO 1133
Total MS 201 B N HDPE blow molding
FINATHENE® MS 201 B N is a high density polyethylene produced by a low pressure slurry polymerization process. FINATHENE® MS 201 B N has been developed for the blow molding of Plastic Fuel Tanks a..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg
8.0 g/10 min

@Load 47.6 lb
ASTM D 1238
Total Xsene® XS10 B HDPE, pipe, injection molding
FINATHENE® XS10 B is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS10 B is a high performance black compound speci..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg
8.0 g/10 min

@Load 47.6 lb
ASTM D 1238
Total Xsene® XS10 H HDPE, pipe, injection molding
FINATHENE® XS 10 H is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 H is a high performance dark blue compound..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg,
Temperature 190 °C
8.0 g/10 min

@Load 47.6 lb,
Temperature 374 °F
Condition F; ASTM D1238
Formosa Plastics Formolene® E924ND Film HDPE
High Molecular Weight High Density Polyethylene (HMW-HDPE) for Film Extrusion Formolene® E924ND is a bi-modal HMW-HDPE resin designed for high dart impact strength and good processing characteristi..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg,
Temperature 250 °C
8.0 g/10 min

@Load 47.6 lb,
Temperature 482 °F
BASF Luranyl® KR 2460/3 Polyphenylene Ether + Styrene-Butadiene Blend
Flame retardant grade with very high heat resistance; used for precision parts and where the material must withstand high injection temperatures (e.g. heater-fan impellers).Data was collected by ISO..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg
8.0 g/10 min

@Load 47.6 lb
ISO 1133
Total Finathene® 53080 HDPE, blow molding, sheet  (discontinued **)
Finathene E® 53080 is a high density polyethylene produced by the slurry loop low pressure polymerization process. Finathene E® 53080 has been especially developed for the production of containers..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg,
Temperature 190 °C
8.0 g/10 min

@Load 47.6 lb,
Temperature 374 °F
Condition F; ASTM D1238
Formosa Plastics Formolene® HP4306 Pipe HDPE  (discontinued **)
High Density Hexene Copolymer Formolene® HP4306 is a high performance copolymer that is designed for the most demanding requirements of pressure pipe applications. It is designed specifically for l..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg
8.0 g/10 min

@Load 47.6 lb
ASTM D 1238
Total Xsene® XS10 Orange YCF HDPE, pipe
FINATHENE® XS 10 ORANGE YCF is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 ORANGE YCF is a high performance ..
High Load Melt Index 8.0 g/10 min

@Load 21.6 kg
8.0 g/10 min

@Load 47.6 lb
ASTM D 1238
Total Finathene® SI 508 HDPE blow molding  (discontinued **)
Finathene® SI 508 is part of a new generation of high density ethylene-hexene copolymers produced by the slurry loop low pressure polymerization process. Finathene® SI 508 is a high molecular weig..