Polymer Property : Environmental Stress Crack Resistance = 3.0 hour Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Environmental Stress Crack Resistance <= 3.0 hour
<= 3.0 hour
F-50; 10% Igepal Cond. B; ASTM D-1693
ExxonMobil Escorene® HD-6908 HDPE, Injection Grade  (discontinued **)
Data Provided by Exxon Chemical Canada.Characteristics: Excellent Stiffness, Good ImpactUses: Crates, Pails, Industrial containers
Environmental Stress Crack Resistance <= 3.0 hour
<= 3.0 hour
Cond. B, 10%; ASTM D1693
ExxonMobil HD 6714.17 Injection Molding Resin  (discontinued **)
HD 6714 is a narrow molecular weight hexene copolymer designed for outstanding processability to maximize injection molding productivity. This resin is ideally suited for thin wall multicavity part..
Environmental Stress Crack Resistance <= 3.0 hour
<= 3.0 hour
Cond. B, 10%; ASTM D1693
ExxonMobil HD 6908.18 Injection Molding Resin  (discontinued **)
HD 6908 is a homopolymer with outstanding stiffness with a good balance of processability and cold temperature impact performance. This resin is ideally suited for articles requiring very high stif..
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 107-276 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 107-277 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 107-278 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 107-279 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 108-276 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 108-277 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 158-280 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 158-281 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 162-280 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 162-281 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance 3.0 hour
3.0 hour
Cond. B, 10%; ASTM D 1693
Ineos J60-800-178 HDPE
A high density polyethylene homopolymer. It has a narrow molecular weight distribution and is intended for the injection molding of screw caps dedicated to the packaging of still and sparkling water..
Environmental Stress Crack Resistance 3.0 hour
3.0 hour
Condition B, 10%, F50; ASTM D1693
Ineos T60-800 HDPE
Ineos T60-800 is a high density polyethylene homopolymer. This narrow molecular weight distribution resin is a product of Ineos' innovative technology. Parts fabricated from this material exhibit ..
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 108-278 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Kazanorgsintez 108-279 Low Density Polyethylene Composition with Improved Processibility
Production Method: Compositions are produced from low density polyethylene with additives. Application: Intended for cable core lapping.Information Provided by Kazanorgsintez
Environmental Stress Crack Resistance 3.0 hour
3.0 hour
DSM Method
Iran Petrochemical (PCC) 1922T Low Density Polyethylene
LDPE 1922T - for injection molding with a balance between flow properties and mechanical propertiesApplications: toys, household articles, clamping lids.Information provided by Iran Petrochemical Co..
Environmental Stress Crack Resistance 3.0 hour

@Pressure 3.50 MPa
3.0 hour

@Pressure 508 psi
ISO CD 16770
Iran Petrochemical (PCC) BL 3VD HH 4765 High Density Polyethylene
BL3VD is a high density polyethylene with 1-Butene as co monomer. It is very high density and stiffness, good ESCR, high flowability and impact strength.Applications: small blow molding, bottles, c..
Environmental Stress Crack Resistance >= 3.0 hour
>= 3.0 hour
Condition B, F50; ASTM D1693
IRPC Polimaxx Polene V1160 High Density Polyethylene
CHARACTERISTICS: GOOD FLOWABILITYAPPLICATIONS: INJECTION MOLDING FOR LIGHT WEIGHT HOUSEHOLDS, TOYS, FOOD CONTAINERS, COSMETICS CLOSURES, DISPOSABLE ARTICLES, LARGE MOLDING AND COMPLICATED PARTS
Environmental Stress Crack Resistance 3.0 hour
3.0 hour
F<sub>0</sub>; ASTM D1693/B
Reliance Industries Reclair M24300 Polyethylene
High flow Linear Low Density Polyethylene grade. Reclair M24300 is butene comonomer based, with optimum levels of antioxidants.Characteristics:narrow molecular weight distribution, good fluidity, ..