Polymer Property : Melt Flow = 9.3 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 9.3 g/10 min

@Load 5.00 kg,
Temperature 250 °C
9.3 g/10 min

@Load 11.0 lb,
Temperature 482 °F
ASTM D 1238
SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Europe-Africa-Middle East)
Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup..
Melt Flow 9.3 g/10 min

@Load 5.00 kg,
Temperature 250 °C
9.3 g/10 min

@Load 11.0 lb,
Temperature 482 °F
ASTM D 1238
SABIC Innovative Plastics Xenoy® X3108UV PBT+PC (Asia Pacific)
Unreinforced, UV-stabilized, flame retardant, impact modified PBT+PC with V0 at 0.8mm thickness. For interior and exterior applications like wall switches and electrical enclosures.This data was sup..
Melt Flow 9.3 g/10 min

@Load 21.6 kg,
Temperature 190 °C
9.3 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Braskem GM9450F HDPE Blown Film Extrusion Polyethylene
HDPE GM9450F is a high-density polyethylene developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and e..
Melt Flow 9.3 g/10 min

@Load 21.6 kg,
Temperature 190 °C
9.3 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Braskem Green PE SGM9450F Blow Film Extrusion and Cast Film Extrusion High Density Polyethylene
Description: SGM9450F is a high-density polyethylene, developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tena..