Polymer Property : Melt Flow = 2.8 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 2.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Polimeri Europa Eraclene® ML 70 U High Density Polyethylene - Injection Molding
Eraclene ML 70 U is a gas phase high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.This grade has a narrow molecular weight distribution. It combin..
Melt Flow 2.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Polimeri Europa Eraclene® ML 74 High Density Polyethylene - Injection Molding
Eraclene ML 74 is a high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.Its narrow molecular weight distribution leads to high mechanical properties ..
Melt Flow 2.8 g/10 min

@Load 5.00 kg,
Temperature 190 °C
2.8 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ASTM D1238
SABIC B4660/B4660AB High Density Polyethylene for Blow Molding
Product Description: B4660 series grades are medium molecular weight High Density Polyethylene homopolymer for blow molding applications. They are primarily designed for imparting high rigidity, t..
Melt Flow 2.8 - 3.4 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.8 - 3.4 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PE 4133Q (33403) Medium Density Polyethylene
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Melt Flow 2.8 - 3.4 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.8 - 3.4 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1283/L
NIZHNEKAMSKNEFTEKHIM PE 5118Q (18603) Linear Low Density Polyethylene
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
Melt Flow 2.8 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.8 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Ravago Manufacturing Americas Hybrid S466 ABS + Polycarbonate Alloy
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Rava..
Melt Flow 2.8 g/10 min

@Load 5.00 kg,
Temperature 190 °C
2.8 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ASTM D1238
SABIC BM6246LS High Density Polyethylene for Blow Molding
Product Description: BM6246LS grade is a medium molecular weight High Density Polyethylene homopolymer for blow molding applications. It is primarily designed for imparting high rigidity, toughnes..
Melt Flow 2.8 g/10 min

@Load 5.00 kg
2.8 g/10 min

@Load 11.0 lb
ISO 1133
Total Lacqtene® 2007 TN 61 HDPE pipe  (discontinued **)
LACQTENE® 2007 TN 61 is a high density homopolymer polyethylene produced by the gas phase polymerization process.LACQTENE® 2007 TN 61 is best processed between 190 and 230°C.Information provided ..
Melt Flow 2.8 g/10 min

@Load 5.00 kg,
Temperature 200 °C
2.8 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Chi Mei Kibisan® PN-117 SAN
Injection Molding
Melt Flow 2.8 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.8 g/10 min

@Load 8.38 lb,
Temperature 446 °F
Procedure A Condition I; ASTM D1238
Diamond Polymers ASA T-120
Description: ASA Weatherable Polymer, Injection Molding Grade, High Heat ResistanceInformation provided by Diamond Polymers, Inc.
Melt Flow 2.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Polimeri Europa Eraclene® ML 70 High Density Polyethylene - Injection Molding
Eraclene ML 70 is a high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.Its narrow molecular weight distribution leads to high mechanical properties ..