Polymer Property : Melt Flow = 0.10 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	0.10 g/10 min @Load 2.16 kg	0.10 g/10 min @Load 4.76 lb	ISO 1133
Total Lacqtene® 2001 PBK 44 HDPE pipe (discontinued **) LACQTENE® 2001 PBK 44 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2001 PBK 44 is a black compound especially developed for s..
Melt Flow	0.10 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.10 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ISO 1133
Iran Petrochemical (PCC) MF3313 High Density Polyethylene MF3313 is a high molecular weight high density polyethylene . Applications: extrusion, film, blown, bags, and density modifies.Information provided by Iran Petrochemical Commercial Co.
Melt Flow	0.10 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.10 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ISO 1133
Iran Petrochemical (PCC) MF3713 High Density Polyethylene MF3713 is a high molecular weight high density polyethylene.Applications: bags, products for use in property modification.Information provided by Iran Petrochemical Commercial Co.
Melt Flow	<= 0.10 g/10 min @Load 2.16 kg, Temperature 230 Â°C	<= 0.10 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133
Kuraray SEPTONÂ® S4033 Thermoplastic Rubber SEPTONÂ® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTONÂ® resins are hydrogenated styrenic block copolymers, which exhi..
Melt Flow	<= 0.10 g/10 min @Load 10.0 kg, Temperature 200 Â°C	<= 0.10 g/10 min @Load 22.0 lb, Temperature 392 Â°F	ISO 1133
Kuraray SEPTONÂ® S4033 Thermoplastic Rubber SEPTONÂ® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTONÂ® resins are hydrogenated styrenic block copolymers, which exhi..
Melt Flow	0.10 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.10 g/10 min @Load 4.76 lb, Temperature 374 Â°F	GB3682
JPJ Technologies HDPE Pipe Grade Information provided by JPJ Technologies
Melt Flow	0.10 g/10 min @Load 5.00 kg, Temperature 190 Â°C	0.10 g/10 min @Load 11.0 lb, Temperature 374 Â°F
Kazanorgsintez PE2NT 11-9 High Density Polyethylene Composite Production Method: Copolymerization of eythylene at low pressure in presence of complex catalysts using gaseous-phase method. Application: Composition is intended to be processed into pressure p..
Melt Flow	0.10 g/10 min @Load 5.00 kg, Temperature 190 Â°C	0.10 g/10 min @Load 11.0 lb, Temperature 374 Â°F	ISO 1133
Iran Petrochemical (PCC) BL7 HM 6255 High Density Polyethylene BL7 (HM 6255) is a high density polyethylene with Butene-1 as comonomer. It is a special grade for particularly high requirements like low temperature impact strength and stacking, good stress crack..
Melt Flow	<= 0.10 g/10 min @Load 2.16 kg, Temperature 230 Â°C	<= 0.10 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133
Kuraray SEPTONÂ® S8004 Thermoplastic Rubber SEPTONÂ® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTONÂ® resins are hydrogenated styrenic block copolymers, which exhi..
Melt Flow	<= 0.10 g/10 min @Load 10.0 kg, Temperature 200 Â°C	<= 0.10 g/10 min @Load 22.0 lb, Temperature 392 Â°F	ISO 1133
Kuraray SEPTONÂ® S8004 Thermoplastic Rubber SEPTONÂ® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTONÂ® resins are hydrogenated styrenic block copolymers, which exhi..
Melt Flow	0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Unipetrol PE HD LITEN® FB 10 HDPE Made for tubular film applications.Information provided by Unipetrol RPA
Melt Flow	<= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Topas Advanced Polymers TOPAS® 5013F-04 Cyclic Olefin Copolymer (COC) TOPAS® 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity ..
Melt Flow	0.10 g/10 min @Load 2.16 kg	0.10 g/10 min @Load 4.76 lb	ISO 1133
Total HP 401 MDPE, pipe, cable, sheet FINATHENE® HP 401 is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low-pressure slurry polymerization process. FINATHENE® HP 401 is a black high densit..
Melt Flow	0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Chevron Phillips Marlex® HP076 High Density Polyethylene, Pipe Grade This hexene copolymer is tailored for pipe applications that require:Good melt strengthGood pipe stiffnessOutstanding ESCRTypical corrugated pipe applications for HP076 include:Culverts and storm se..
Melt Flow	<= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
ExxonMobil HDPE BU46-055 High Density Polyethylene Resin Product Description: BU46-055 is a high molecular weight, high density polyethylene copolymer which contains a UV inhibitor. It possesses a combination of excellent processability, outstanding melt ..
Melt Flow	<= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
ExxonMobil HDPE BU46-060 High Density Polyethylene Resin Product Description: BU46-060 is a high molecular weight, high density polyethylene copolymer which contains a UV inhibitor. It possesses a combination of excellent processability, outstanding melt ..
Melt Flow	<= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
ExxonMobil HDPE HYA021L High Density Polyethylene Resin Product Description: HYA021L is a molecular weight, high-density polyethylene copolymer. This resin has superior stress crack resistance, high impact strength and good rigidity.Availability: Latin A..
Melt Flow	0.10 g/10 min @Load 5.00 kg, Temperature 200 °C	0.10 g/10 min @Load 11.0 lb, Temperature 392 °F	Procedure A Condition G; ASTM D1238
Diamond Polymers ABS 3501 GF-30 Description: Reinforced Grade, 30%Glass FilledInformation provided by Diamond Polymers, Inc.
Melt Flow	0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Diamond Polymers DIAMALOY WPE 2000 Wood Filled HDPE Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Melt Flow	0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Diamond Polymers NPP50-1111 TF20 20% Talc Filled White High Density Polyethylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Melt Flow	0.10 g/10 min @Load 2.16 kg	0.10 g/10 min @Load 4.76 lb	ISO 1133
Total Lacqtene® 2001 TBK 46 HDPE pipe (discontinued **) LACQTENE® 2001 TBK 46 is a high density polyethylene produced by the gas phase polymerization process. LACQTENE® 2001 TBK 46 is a black compound especially developed for pressure pipe for gas and ..
Melt Flow	0.10 g/10 min @Load 2.16 kg	0.10 g/10 min @Load 4.76 lb	ISO 1133
Total Lacqtene® 2001 TN 46 HDPE pipe (discontinued **) LACQTENE® 2001 TN 46 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2001 TN 46 is used for sewage pipe, smooth protective condu..
Melt Flow	0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Unipetrol PE HD LITEN® VL 29 HDPE Extrusion and pipe applications.Information provided by Unipetrol RPA
Melt Flow	>= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	>= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis Borstar® HE3490-LS Black High Density Polyethylene for Pressure Pipes Borstar HE3490-LS is a black, bimodal, high density polyethylene classified as an MRS 10.0 material (PE100) produced by the advanced Borstar technology. Well dispersed carbon black gives outstanding..