Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
Polimeri Europa Edistir N 1782 Polystyrene General purpose polystyrene with good flow and high heat resistance. Suggested for direct gassing extrusion of heavy gage insulating boards (XPS) and in blend with high concentration of clear SBS f.. |
|||
Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Polimeri Europa Riblene® MP 30 R Low Density Polyethylene - Injection Molding Riblene MP 30 R is a medium fluidity low density polyethylene resin (LDPE).Parts made by Riblene MP 30 R are characterized by a medium rigidity.Main Applications: Riblene MP 30 R is suitable for in.. |
|||
Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® 500 PC 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. |
|||
Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® 500 PC (Asia Pacific) 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. |
|||
Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® EXL4019 PC Lexan* EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers im.. |
|||
Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® EXL4019 PC (Asia Pacific) Lexan* EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers im.. |
|||
Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® LUX2619 PC (Europe-Africa-Middle East) Lexan* LUX2619 Polycarbonate resin is an extrusion grade. It is UL94 V-2 rated at 1.5 mm. It was designed for high light reflectance. |
|||
Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® OQ2720 PC (Asia Pacific) Ophthalmic/safety lens market. OQ2xxx series in all transparent tints. Dedicated equipment, stringent production control conditions. |
|||
Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
Network Polymers 702 Polystyrene Description: Ignition RetardantInformation provided by Network Polymers Inc. |
|||
Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 190 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 374 °F |
|
Total Finaprene® 507 Styrene-Butadiene TPE Copolymer
(discontinued **) Styrene-Butadiene CopolymerDescription: Finaprene® 507 is a thermoplastic elastomer type radial styrene-butadiene block copolymer. Thanks to its high styrene content, Finaprene® 507 provides exce.. |
|||
Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
old Condition G; ASTM D1238 |
Ineos Nova PS 2521 Crystal Polystyrene
(discontinued **) Information provided by Nova ChemicalsINEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets. |
|||
Melt Flow | 7.5 g/10 min | 7.5 g/10 min | Condition G |
Ineos Nova 2510 General Purpose Crystal Polystyrene
(discontinued **) High speed molding, Improved crack resistance, USP Class VIApplications: Cutlery, Light louvers, RazorsExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the phy.. |
|||
Melt Flow | 7.5 g/10 min | 7.5 g/10 min | Condition G |
Ineos Nova 2511 General Purpose Crystal Polystyrene
(discontinued **) High speed molding, Improved crack resistance, USP Class VIApplications: Cutlery, Light louvers, RazorsExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the phy.. |
|||
Melt Flow | 7.5 g/10 min | 7.5 g/10 min | Condition I; ASTM D1238 |
Plaskolite Optix® PL-76 Acrylic Resin
(discontinued **) Injection/extrusion pellets. Medium heat resistance with higher flow than PL-52 pellets.Data provided by the manufacturer, Plaskolite, Inc. |
|||
Melt Flow | 7.5 g/10 min @Load 2.61 kg, Temperature 190 °C |
7.5 g/10 min @Load 5.75 lb, Temperature 374 °F |
ASTM D1238 |
LG Chemical LUTENE LB7500 LDPE Extrusion Coating Description: LUTENE LB7500 is mainly intended for extrusion coating and can be processed at high speed uniform thickness and width. LUTENE LB7500 is also noted for the excellent adhesion to porous a.. |
|||
Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 6 cm<sup>3</sup>/10min.; ISO 1133 |
Mitsubishi Xantar® G2F 23 UR Polycarbonate-10% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Multibase Multi-Flex® A 7202 MR TPE Thermoplastic Elastomer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase |
|||
Melt Flow | 7.5 g/10 min @Load 6.60 kg, Temperature 337 °C |
7.5 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
SABIC Innovative Plastics ULTEM AUR200G6 PEI (Europe-Africa-Middle East) The data listed in this data sheet are the lower specification limits, apart from the MFR, CTE, HDT at 1.8 MPa, Density, Tensile strain, Water Absorption, Thermal Conductivity and Shrinkage which ar.. |
|||
Melt Flow | 7.5 g/10 min @Load 6.60 kg, Temperature 337 °C |
7.5 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
SABIC Innovative Plastics LNP STAT-KON Ultem_UC1200 PEI (Europe-Africa-Middle East) LNP* Stat-kon* Ultem_UC1200 compound is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications. |
|||
Melt Flow | 7.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® SL-0110 ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 7.5 g/10 min @Load 10.0 kg, Temperature 230 °C |
7.5 g/10 min @Load 22.0 lb, Temperature 446 °F |
ISO 1133 |
Polyram RamClean™ 800 Ethylene Propylene Compound Purging Agent Ethylene propylene compound purging agent for extruders/injection molding machines.Information provided by Polyram. |
|||
Melt Flow | 7.5 g/10 min @Load 21.6 kg, Temperature 190 °C |
7.5 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Total HDPE XT10 N High Density Polyethylene - Pipe Resin Polyethylene: High molecular weight, bimodal pipe resin.Characteristics:Outstanding high temperature creep rupture strengthExceptional slow crack growth resistanceExcellent resistance to rapid crac.. |
|||
Melt Flow | 7.5 g/10 min @Load 21.6 kg, Temperature 190 °C |
7.5 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Total HDPE XT25N High Density Polyethylene, Pipe Resin Polyethylene: High molecular weight, bimodal pipe resin. PPI TR4 designation PE4710 /PE100 for demanding installations. Every batch certified to meet 2500 hrs PENT according to ASTM F1473.Charact.. |
|||
Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Chevron Phillips K-Resin® KR03NW Styrene-Butadiene Copolymer, Sheet Grade Styrene-Butadiene Copolymer. No wax (NW) form of K-Resin® KR03 to facilitate printing.Customer Benefits: This SBC is easily processed by injection molding or sheet extrusion and molded parts give .. |
|||
Melt Flow | 7.5 g/10 min | 7.5 g/10 min | ExxonMobil Method |
ExxonMobil EXACT™ 3139 Plastomer for Cast Film Applications Product Description: Exact 3139 is an ethylene-based hexene plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. Exact 3139 is designed for both monolayer and multilayer coe.. |
|||
Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
ExxonMobil PP1013H1 Polypropylene Homopolymer Product Description: A homopolymer resin that meets certified requirements for use in Medical and Pharmaceutical applications.Availability: Europe and North America Features:Autoclave SterilizableE.. |
|||
Melt Flow | 7.5 g/10 min | 7.5 g/10 min | ISO 1133 |
Domo 2600M Polypropylene Copolymer Information provided by Domo. |
|||
Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Barlog Plastics KEBAFORM C 901 TF POM Copolymer unreinforced, improved wear and friction POMInformation provided by BARLOG plastics GmbH. |
|||
Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D-1238 |
Chevron Phillips K-Resin® KR03BR SBC
(discontinued **) K-Resin® Styrene-Butadiene Copolymer (SBC)Applications:BottlesMolded boxes and containersMedical devicesPortion packagesBlister packagingFeatures:Good stiffnessGood formabilityGood toughnessExcelle.. |