Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A; ASTM D1238 |
PolyOne Maxxam™ DP-8928-2-1000 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A; ASTM D1238 |
PolyOne Maxxam™ DP-8928-2-8001 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
Melt Flow | 7.3 g/10 min @Load 5.00 kg, Temperature 190 °C |
7.3 g/10 min @Load 11.0 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
PolyOne Elastamax™ EG-9172 Thermoplastic Elastomer (TPE) The Elastamax™ EG 9100 Series is a new family of olefin-based TPE compounds offering outstanding elastomeric performance in a lightweight and easy to process material. The EG 9100 Series of compoun.. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® 21E553 Adhesive Resin
(discontinued **) Bynel® Series 2100 resins are anhydride-modified ethylene acrylate resins. They contain a temperature stable ester that makes them functional in high temperature coextrusions. They are available in.. |
|||
Melt Flow | 7.3 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.3 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® ML1665 PC Polycarbonate for aircraft applications requiring FAR 25.853a compliance. For extrusion and injection molding applications. Opaque colors only |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ineos H07B-01 Polypropylene Homopolymer This is a polypropylene homopolymer for cast film applications that require antiblock additives and nucleation. This resin meets the requirements of the U.S. Food and Drug Administration as specifi.. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ineos H07N-00 Polypropylene Homopolymer Grade H07N-00 is a barefoot polypropylene homopolymer with nucleation designed for extrusion processing. This resin meets the requirements of the U.S. Food and Drug administration as specified in 12.. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ineos Innovene H07B-00 Polypropylene Homopolymer Extrusion. Features: No Slip, Antiblock.Applications: Cast filmTypical property data below from injection molded samples. |
|||
Melt Flow | 7.3 g/10 min | 7.3 g/10 min | ISO 1133 |
Lucite International Diakon® CLG902 Acrylic Polymer Information provided by Lucite International |
|||
Melt Flow | 7.3 g/10 min | 7.3 g/10 min | ISO 1133 |
Lucite International Diakon® CLG902L Acrylic Polymer Information provided by Lucite International |
|||
Melt Flow | 7.3 g/10 min | 7.3 g/10 min | ISO 1133 |
Lucite International Diakon® CLG902LX Acrylic Polymer Information provided by Lucite International |
|||
Melt Flow | 7.3 g/10 min | 7.3 g/10 min | ISO 1133 |
Lucite International Diakon® LG702 Acrylic Bead Polymer, High Transparency PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite Inte.. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Westlake EBAC® SP1806 17.5%, Ethylene-Methyl Acrylate Copolymer Description: Westlake EBAC® SP1806 is an ethylene butyl acrylate copolymer designed for extrusion coating and laminating. SP1806 can also be compounded as an impact modifier or used in highly fill.. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238, ISO 1133 |
DuPont™ Appeel® 20D855 Ethylene Acrylate DuPont™ Appeel 20D855 is a modified ethylene acrylate resin designed to function as a sealing layer for lidding applications. It is most often suggested to provide peelable seals over a broad tempe.. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
ExxonMobil PP9513 Polypropylene Homopolymer Product Description: A random copolymer resin designed for non-oriented film.Availability: North America Features:Controlled RheologyEthylene Oxide SterilizableUses: BagsCast FilmHeavy-duty BagsPac.. |
|||
Melt Flow | 7.3 g/10 min @Load 1.00 kg, Temperature 235 °C |
7.3 g/10 min @Load 2.20 lb, Temperature 455 °F |
|
Arkema Group Pebax® MV 1041 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 60 shore D breathable (high permeability to H2O vapor,CO2,O2) permanent antistatic grade Applications: breathable films (medical, textile....)ISO data provided .. |
|||
Melt Flow | 7.3 g/10 min @Load 1.00 kg, Temperature 235 °C |
7.3 g/10 min @Load 2.20 lb, Temperature 455 °F |
|
Arkema Group Pebax® MV 1041 SN 01 Polyether Block Amide (PEBA) (Dry) POLYETHER BLOCK AMIDE (PEBA) hardness 60 shore D breathable (high permeability to H2O vapor,CO2,O2) permanent antistatic grade Applications: breathable films (medical, textile....)ISO data provided .. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
Braskem HD3000N HDPE Cast Film Extrusion Polyethylene Homopolymer HD3000N is a high-density polyethylene, narrow molecular weight homopolymer produced by the solution process for cast film extrusion. It offers high processability, stiffness, and good impact resist.. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Azoty Tarnow™ TARNOFORM 300 GF2 POM 10% glass fiber reinforced injection molding grade, suitable for applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A... |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
Braskem IA59 HDPE Injection Molding Polyethylene Homopolymer IA59 is a high-density polyethylene, narrow molecular weight homopolymer produced by the solution process for injection molding applications. It offers high processability and low warpage and contai.. |
|||
Melt Flow | 7.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
7.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
Arkema Group Oroglas® V 920 Acrylic, Injection Molding Grade
(discontinued **) OROGLAS V 920 is an injection molding grade with a good balance of properties :Superior flow with medium thermal resistance.The processing of OROGLAS V 920 is easy in terms of injection molding, mo.. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ineos H07B-00 Polypropylene Homopolymer This is a polypropylene homopolymer for cast film applications that require antiblock additives. This resin meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 17.. |
|||
Melt Flow | 7.3 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.3 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ineos H07D-00 Polypropylene Homopolymer Grade H07D-00 is a polypropylene homopolymer for cast film applications that require slip and antiblock additives. This resin meets the requirements of the Food and Drug Administration as specified .. |
|||
Melt Flow | 7.3 - 8.3 g/10 min @Load 1.20 kg, Temperature 250 °C |
7.3 - 8.3 g/10 min @Load 2.65 lb, Temperature 482 °F |
|
Kazanorgsintez PC-075D Polycarbonate Production Method: Obtained by means of polycondensation method. Application: Intended for manufacture of optical products by method of die-casting (including CD, DVD, and other discs), as well .. |