- Polymer Property : Melt Flow = 6.1 g/10 min
Polymer Property : Melt Flow = 6.1 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 6.1 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.1 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ExxonMobil HD 6761.17 Injection Molding Resin
(discontinued **) HD 6761 is a narrow molecular weight hexene copolymer designed for good processability and excellent balance of ESCR, Toughness, and Stiffness properties. This resin is ideally suited for a heavy-d.. |
|||
| Melt Flow | 6.1 g/10 min | 6.1 g/10 min | ASTM D1238 |
| LyondellBasell Alathon® M4661 High Density Polyethylene ApplicationsALATHON M 4661, formerly known as LYHD 060, exhibits excellent impact, warp and environmental stress crack resistance. Typical applications are closures, institutional seating and consum.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 5 cm<sup>3</sup>/10min.; ISO 1133 |
| Mitsubishi Xantar® SF 22 Polycarbonate Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Melt Flow | 6.1 - 7.5 g/10 min | 6.1 - 7.5 g/10 min | ASTM D1238-04 |
| Ipiranga Petrochem GP 100 BK HDPE The resin GP 100 BK is a high density polyethylene compounding with high molar mass, specially developed for the manufacturing of extruded pipes for gas distribution. It is produced with bimodal tec.. |
|||
| Melt Flow | 6.1 - 7.5 g/10 min | 6.1 - 7.5 g/10 min | ASTM D1238-04 |
| Ipiranga Petrochem GP 100 OR HDPE The resin GP 100 OR is a high density polyethylene compounding with high molar mass, specially developed for the manufacturing of extruded pipes for gas distribution. It is produced with bimodal tec.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® 1804 Polycarbonate MVR (300 °C/1.2 kg) 6.0 cm3/10 minhigh viscosityUV stabilizedoptimized for low plate-outimproved flammabilityUL 94 V-2/1.5 mm and 3.0 mmavailable in transparenttranslucent and opaque colorssolid sh.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® 3103 MAS157 Polycarbonate ISO 7391-PC,EL,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minExtrusionHigh viscosityUV stabilizedAvailable in color code 550115 onlySolid sheetCorrugated sheetPreprocessingMax. Water conte.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® 3106 Polycarbonate ISO 7391-PC,M,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minFood contact qualityHigh viscosityGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CExtrusionAvailable.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® 3107 Polycarbonate ISO 7391-PC,MLR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minGeneral purposeHigh viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in transpare.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® 3156 Polycarbonate ISO 7391-PC,MR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minFood contact qualityHigh viscosityEasy releaseGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CExtru.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® 6585 Polycarbonate, Flame Retardant Grade ISO 7391-PC,MFR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minFlame retardantUL 94V-0/1.2 mm5VA/3.0 mm and 5VB (WT) /2.0 mmHigh viscosityEasy releaseInjection molding - Melt temperature 28.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® LQ3147 Polycarbonate ISO 7391-PC,MLR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minOptical lensHigh viscosityUV stabilizedEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in clear tints .. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® LTG3123 Polycarbonate PreprocessingMax. Water content |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® Rx1805 Polycarbonate ISO 7391-PC,M,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minMedical devicesLipid resistantsuitable for sterilization with high-energy radiationComplies with the requirements of FDA-modifie.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® 1243 Polycarbonate ISO 7391-PC,ELS,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minExtrusionHigh viscosityBranchedUV stabilizedEasy releaseAvailable in color code 550111onlyMulti wall sheet/profilesPreprocessi.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® DP1-1825* Polycarbonate, Impact Grade Developmental productISO 7391-PC,MP,(,,)-09-9MVR (300 °C/1.2 kg) 6.0 cm3/10 minImpact modifiedHigh viscosityInjection molding - Melt temperature 280 - 320 °CAvailable in opaque colors onlyPreproce.. |
|||
| Melt Flow | 6.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Covestro Makrolon® LQ3187 Polycarbonate ISO 7391-PC,MLR,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minOptical lensHigh viscosityUV stabilizedUV 400 cut offEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable i.. |
|||
| Melt Flow | 6.1 g/10 min | 6.1 g/10 min | Condition D; ASTM D 1238 |
| CPT C-Flex® R70-190 Opaque Biocompatible TPE C-Flex® is a family of patented thermoplastic elastomers which range in hardness from 5 shore A to 95 shore A. C-Flex® TPE's are biocompatible polymer blends which meet or exceed the current.. |
|||
| Melt Flow | 6.1 g/10 min @Load 5.00 kg, Temperature 300 °C |
6.1 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| SABIC Innovative Plastics NORYL PX2944 PPE+HIPS (Asia Pacific) PPE/PS, GF20%, high heat, non-FR |
|||