Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 5.4 g/10 min | 5.4 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE A 9305 BLK This product was developed for one shot airbag covers with improved stiffness and low temperature resistance. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Melt Flow | 5.4 g/10 min @Load 1.20 kg, Temperature 280 °C |
5.4 g/10 min @Load 2.65 lb, Temperature 536 °F |
ISO 1133:1997 |
Nanocyl PLASTICYL™ PA1503 Polyamide 6 with 3 wt% of Multi-Wall Carbon Nanotubes PLASTICYL™ is a family of Multi-Wall Carbon Nanotube (MWNT) thermoplastic concentrates for applications requiring superior electrical conductivity and electrostatic discharge (ESD) properties. PLA.. |
|||
Melt Flow | 5.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
cm³/10 min |
Polimeri Europa EDISTIR N1670 Polystyrene
(discontinued **) Symbol according to ISO 1043-1: PS Designation: Thermoplastic ISO 1622-PS,E,095-06 General purpose polystyrene with good flow and good heat resistance. Recommended for extrusion in blend with HIP.. |
|||
Melt Flow | 5.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
cm³/10 min |
Polimeri Europa EDISTIR N1671 Polystyrene
(discontinued **) Symbol according to ISO 1043-1: PS Designation: Thermoplastic ISO 1622-PS,M,095-06 General purpose polystyrene with good flow and good heat resistance for rapid set-up. To be used in injection mol.. |
|||
Melt Flow | 5.4 - 6.6 g/10 min @Load 21.6 kg, Temperature 190 °C |
5.4 - 6.6 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
LG Chemical SEETEC PB150 HDPE Features: This high molecular weight, hexane copolymer is tailored for high impact blow-molded containers that require:Excellent processabilityHigh impact strength at low temperatureOutstanding stre.. |
|||
Melt Flow | 5.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Solvay Specialty Polymers Solef® 20808 Polyvinylidene Fluoride (PVDF) Copolymer; Low ViscosityAdditional Properties: Abrasion Resistance - ASTM D4060 29.0 mg; Coefficient of Friction - ASTM D1894 0.280; Coefficient of Linear Thermal Expansion - ASTM D696 1.4E-4 to 1.6.. |
|||
Melt Flow | 5.4 g/10 min | 5.4 g/10 min | JIS K7210 |
Stellarchem AB845EM TPE Compound This grade of Stellarchem TPE is shear dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It's a soft, elastomeric polyolefin based, complete.. |
|||
Melt Flow | 5.4 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.4 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® GR-4030 ABS, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 5.4 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.4 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 5.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® VH-0800 ABS, Unreinforced FR Flame-retardant ABS with excellent weather resistance that is used in the exterior of OA devices such as monitors, printers, fax machines, duplicators etc.Information provided by Samsung Cheil Indus.. |
|||
Melt Flow | 5.4 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.4 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® GR-4030 ABS, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 5.4 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.4 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 5.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Samsung Cheil Industries Starex® VH-0800 ABS, Unreinforced FR Flame-retardant ABS with excellent weather resistance that is used in the exterior of OA devices such as monitors, printers, fax machines, duplicators etc.Information provided by Samsung Cheil Indus.. |
|||
Melt Flow | 5.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Teknor Apex TEKRON® 4200-70 Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Melt Flow | 5.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM Data |
Dow Retain® PS-4578 Polystyrene Data provided by Dow Chemical. |
|||
Melt Flow | 5.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
BASF Novolen® 2800 J Polypropylene Injection molded partsData was collected by ISO methods and provided by BASF. |
|||
Melt Flow | 5.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont™ Surlyn® 1652SR Zinc Ionomer Resin for Cast Film and Extrusion Coating Surlyn® 1652SR is an ionomer resin available for use in cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylene resi.. |