Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Melt Flow = 45 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 35 - 45 g/10 min

@Load 2.16 kg,
Temperature 230 °C
35 - 45 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238/L
NIZHNEKAMSKNEFTEKHIM PP 1365S (H22S) Propylene Homopolymer
Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P..
Melt Flow 40 - 45 g/10 min

@Load 2.16 kg,
Temperature 230 °C
40 - 45 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238/L
NIZHNEKAMSKNEFTEKHIM PP 4341S Propylene and Ethylene Copolymer
Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r..
Melt Flow 25 - 45 g/10 min
25 - 45 g/10 min
ASTM D1238
Polymer Resources PC/ABS-FR1-[color]-3 PC Blend, Flame Retardant, Standard Flow, UV Stabilized
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow 25 - 45 g/10 min

@Load 11.6 kg,
Temperature 250 °C
25 - 45 g/10 min

@Load 25.6 lb,
Temperature 482 °F
ASTM D1238
Polymer Resources PPX-SF2 Modified-PPO, Structural Foam Grade, Flame Retardant
Modified-Polyphenylene Oxide, Structural Foam Grade, Standard FlowFeatures: • Flame Retardant • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Foam MoldingNotes: All physical, mec..
Melt Flow 30 - 45 g/10 min

@Load 2.16 kg,
Temperature 250 °C
30 - 45 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ISO 1133
PTS PBT-1100 PBT Resin
Information provided by PTS LLC.
Melt Flow 25 - 45 g/10 min
25 - 45 g/10 min
ASTM D1238
Polymer Resources PPX-SF2 Modified PPO, Structural Foam Grade, Standard Flow  (Unverified Data**)
Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel..
Melt Flow 18 - 45 g/10 min

@Load 2.16 kg,
Temperature 230 °C
18 - 45 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Shanghai Ofluorine T-2 PVDF for Powder Coatings
Description: T-2 PVDF belong to thermoplastic fluorocarbon resin, which has high melt flow rate, low melt viscosity. T-2 PVDF has characteristic of chemical resistance, heat resistance, high mechani..
Melt Flow 25 - 45 g/10 min

@Load 2.16 kg,
Temperature 190 °C
25 - 45 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238 - ISO 1133
DuPont Elvaloy® 741 Ethylene/Vinyl Acetate/Carbon Monoxide Copolymer
Specialized copolymers deliver flexibility, toughness and weatherability to adhesives, plastics, highways and roofing.Availability: GloballyInformation provided by DuPont.
Melt Flow 25 - 45 g/10 min

@Load 2.16 kg,
Temperature 190 °C
25 - 45 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238 - ISO 1133
DuPont Elvaloy® 742 Ethylene/Vinyl Acetate/Carbon Monoxide Copolymer
Specialized copolymers deliver flexibility, toughness and weatherability to adhesives, plastics, highways and roofing.Availability: GloballyInformation provided by DuPont.
Melt Flow 35 - 45 g/10 min

@Load 5.00 kg,
Temperature 235 °C
35 - 45 g/10 min

@Load 11.0 lb,
Temperature 455 °F
3 min; ASTM D1238
ALM PA-616-GS Filled Nylon 12 Prototyping Polymer
50% glass sphere filled material for improved dimensional stability, increased stiffness, and higher temperature applications when compared to unfilled PA.The PA 616-GS can be processed on any laser..
Melt Flow 30 - 45 g/10 min

@Load 2.16 kg,
Temperature 250 °C
30 - 45 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ISO 1133
BLUESTAR PBT 1100
PBT resin is polymerized by pure terephthalic acid (PTA) and 1,4-butanediol (1,4-BDO) through direct esterification. With well-distributed molecular weight and stable quality, PBT resin possesses go..
Copyright © lookpolymers.com All Rights Reserved