Polymer Property : Melt Flow = 35 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	15 - 35 g/10 min @Load 5.00 kg, Temperature 250 °C	15 - 35 g/10 min @Load 11.0 lb, Temperature 482 °F	ASTM D1238
Polymer Resources PC/ABS-FRG5 Flame Retardant PC/ABS Alloy, 5% Glass Reinforced PC/ABS Alloy, Flame Retardant, 5% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr..
Melt Flow	25 - 35 g/10 min @Load 11.6 kg, Temperature 250 °C	25 - 35 g/10 min @Load 25.6 lb, Temperature 482 °F	ASTM D1238
Polymer Resources PPX-GP4-WR Modified-PPO, General Purpose, Wear Resistant Modified-Polyphenylene Oxide, General Purpose, Wear Resistant, 215F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test s..
Melt Flow	25 - 35 g/10 min @Load 2.16 kg, Temperature 250 °C	25 - 35 g/10 min @Load 4.76 lb, Temperature 482 °F	ASTM D1238
Polymer Resources TP-HG40 Polybutylene Terephthalate, 40% Glass Reinforced Alloy Polybutylene Terephthalate, 40% Glass Reinforced AlloyProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informatio..
Melt Flow	15 - 35 g/10 min @Load 5.00 kg, Temperature 250 °C	15 - 35 g/10 min @Load 11.0 lb, Temperature 482 °F	ASTM D1238
Polymer Resources PC/ABS-FR1-[color]-HH Flame Retardant PC/ABS Alloy, Low Flow PC/ABS Alloy, Flame Retardant, Low FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by P..
Melt Flow	30 - 35 g/10 min @Load 2.16 kg, Temperature 230 °C	30 - 35 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman.
Melt Flow	30 - 35 g/10 min	30 - 35 g/10 min	ASTM D1238
A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman.
Melt Flow	30 - 35 g/10 min @Load 2.16 kg, Temperature 230 °C	30 - 35 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman.
Melt Flow	30 - 35 g/10 min	30 - 35 g/10 min	ASTM D1238
A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman.
Melt Flow	30 - 35 g/10 min	30 - 35 g/10 min	ASTM D1238
A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman.
Melt Flow	30 - 35 g/10 min	30 - 35 g/10 min	ASTM D1238
A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman.
Melt Flow	30 - 35 g/10 min @Load 2.16 kg, Temperature 230 °C	30 - 35 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman.
Melt Flow	20 - 35 g/10 min @Load 8.70 kg, Temperature 210 °C	20 - 35 g/10 min @Load 19.2 lb, Temperature 410 °F
Lubrizol Estane® GP 55 DB Thermoplastic Polyurethane Type: Estane® GP 55DB is an aromatic polyester-based thermoplastic polyurethane (TPU).Features: Translucent spherical pellets.Uses: Injection molding partsAvailable in EuropeInformation Provided by..
Melt Flow	15 - 35 g/10 min @Load 8.70 kg, Temperature 210 °C	15 - 35 g/10 min @Load 19.2 lb, Temperature 410 °F
Lubrizol ESTANE® GP52DB Ester Based Thermoplastic Polyurethane Type: Estane® GP 52DB is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided b..
Melt Flow	15 - 35 g/10 min @Load 8.70 kg, Temperature 210 °C	15 - 35 g/10 min @Load 19.2 lb, Temperature 410 °F
Lubrizol ESTANE® GP55DT Ether Based Thermoplastic Polyurethane Type: Estane® GP 55DT is an aromatic polyether-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding parts, animal identification tagsAvailable in ..
Melt Flow	10 - 35 g/10 min @Load 8.70 kg, Temperature 215 °C	10 - 35 g/10 min @Load 19.2 lb, Temperature 419 °F
Lubrizol ESTANE® GP65DE Ester Based Thermoplastic Polyurethane Type: Estane® GP 65DE is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided b..
Melt Flow	20 - 35 g/10 min @Load 8.70 kg, Temperature 217 °C	20 - 35 g/10 min @Load 19.2 lb, Temperature 423 °F
Lubrizol ESTANE® GP72DB Ester Based Thermoplastic Polyurethane Type: Estane® GP 72DB is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding parts, TranslucentAvailable in EuropeInformati..
Melt Flow	10 - 35 g/10 min @Load 8.70 kg, Temperature 195 °C	10 - 35 g/10 min @Load 19.2 lb, Temperature 383 °F
Lubrizol ESTANE® GP85AE Ester Based Thermoplastic Polyurethane Type: Estane® GP 85AE is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided b..
Melt Flow	10 - 35 g/10 min @Load 8.70 kg, Temperature 205 °C	10 - 35 g/10 min @Load 19.2 lb, Temperature 401 °F
Lubrizol ESTANE® GP95AE Ester Based Thermoplastic Polyurethane Type: Estane® GP 95AE is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses:Injection molding partsAvailable in EuropeInformation provided by..
Melt Flow	20 - 35 g/10 min @Load 8.70 kg, Temperature 210 °C	20 - 35 g/10 min @Load 19.2 lb, Temperature 410 °F
Lubrizol ESTANE® GP98AE Ester Based Thermoplastic Polyurethane Type: Estane® GP 98AE is an aromatic polyester-based thermoplastic polyurethane (TPU).Appearance: Translucent spherical pelletsUses: Injection molding partsAvailable in EuropeInformation provided b..
Melt Flow	30 - 35 g/10 min @Load 2.16 kg, Temperature 230 °C	30 - 35 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman.
Melt Flow	30 - 35 g/10 min @Load 2.16 kg, Temperature 230 °C	30 - 35 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman.
Melt Flow	25 - 35 g/10 min @Load 5.00 kg, Temperature 372 °C	25 - 35 g/10 min @Load 11.0 lb, Temperature 702 °F
Daikin NEOFLON EP-610 ETFE Pellets Due to its excellent melt flow properties, NEOFLON ETFE can be processed in the same was as other thermoplastic resins. NEOFLON ETFE is also highly suited to such secondary processes as welding, fl..
Melt Flow	25 - 35 g/10 min	25 - 35 g/10 min	ASTM D1238
Buckeye Polymers BP PPC 0235 BLK Polypropylene Copolymer Product Information: Black Polypropylene Copolymer good for general purpose programs requiring moderate impact resistance.Product Features:Good impact resistanceGood UV resistanceGood chemical resis..
Melt Flow	19 - 35 g/10 min @Load 3.80 kg, Temperature 232 °C	19 - 35 g/10 min @Load 8.38 lb, Temperature 450 °F	ASTM D1238
Arkema Group KYNAR® 710, 710 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness ..
Melt Flow	19 - 35 g/10 min @Load 3.80 kg, Temperature 232 °C	19 - 35 g/10 min @Load 8.38 lb, Temperature 450 °F	ASTM D1238
Arkema Group KYNAR® 711 Polyvinylidene Fluoride Powder Characteristics: White, non-hygroscopic powder. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistan..
Melt Flow	30 - 35 g/10 min	30 - 35 g/10 min	ASTM D1238
A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman.
Melt Flow	30 - 35 g/10 min @Load 2.16 kg, Temperature 230 °C	30 - 35 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
A. Schulman PP 3052X-01 Polypropylene Impact Resistant Copolymer DescriptionPolypropylene PP 3052X-01 is an extra high flow impact resistant copolymer with relatively high stiffness. Information provided by A. Schulman.
Melt Flow	25 - 35 g/10 min	25 - 35 g/10 min	ASTM D1238
Polymer Resources PPX-GP4-WR Modified PPO, Wear Resistant with HDT of 215 F (Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Melt Flow	30 - 35 g/10 min	30 - 35 g/10 min	ASTM D1238
A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman.
Melt Flow	25 - 35 g/10 min	25 - 35 g/10 min	25-35 cm<sup>3</sup>/10 min; Melt Volume Rate
Huntsman IROGRAN® A 85 P 4934 Ether-Based TPU-For Cable Industry TransparentInformation provided by Huntsman