Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 31.2 g/10 min @Load 5.00 kg, Temperature 275 °C |
31.2 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
BASF Ultramid® A3EG10 50% Glass Filled PA66 (Conditioned) Description: 50% glass-fiber reinforced injection-molding grade for technical articles of very high stiffness as well as for electric insulating parts.Information provided by BASF |
|||
Melt Flow | 31.2 g/10 min @Load 5.00 kg, Temperature 275 °C |
31.2 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
BASF Ultramid® A3EG10 50% Glass Filled PA66 (Dry) Description: 50% glass-fiber reinforced injection-molding grade for technical articles of very high stiffness as well as for electric insulating parts.Information provided by BASF |
|||
Melt Flow | 31.2 g/10 min @Load 5.00 kg, Temperature 275 °C |
31.2 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
BASF Ultramid® A3WG10 BK 00564 50% Glass Filled PA66 (Conditioned) Description: 50% glass-fiber reinforced injection-molding grade with high heat aging resistance for technical articles of very high stiffness.Information provided by BASF |
|||
Melt Flow | 31.2 g/10 min @Load 2.16 kg, Temperature 250 °C |
31.2 g/10 min @Load 4.76 lb, Temperature 482 °F |
Calculated from Volume Flow Rate of 24 cm<sup>3</sup>/10min.; ISO 1133 |
DSM Arnite® T06 202 PBT (European and Asian Grade) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |