- Polymer Property : Melt Flow = 3.8 g/10 min
Polymer Property : Melt Flow = 3.8 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Plaskolite West Optix® CP - 75 HID General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
| Melt Flow | 3.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Polimeri Europa Edistir N 2560 Polystyrene High molecular weight general purpose polystyrene with good mechanical strength and good thermal resistance. It is recommended for in-line forming of disposable packaging, for sheet
extrusion in ble.. |
|||
| Melt Flow | 3.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Resirene Resirene® 6220 High Impact Polystyrene Features:Low FlowEasy ProcessingGood GlossHigh ElongationFDA Rating: 21 CFR 177.1640Mechanical StrengthApplications:Extrusion/ ThermoformingDisposablesGPPS/HIPS BlendsRefrigerator PartsInformation p.. |
|||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| NOVA Chemicals Sclair® 8306 UV8D, 8306G UV8D MDPE Rotational Molding Resin
(discontinued **) Features: Balanced combination of toughness, ESCR and processability.Applications: General purpose.Data provided by the manufacturer. |
|||
| Melt Flow | 3.8 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.8 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min. |
| Ineos ABS Centrex® 815 ASA Blend
(discontinued **) Key Features:UnfilledLight stabilized or stable to lightU.V. stabilized or stable to weatherHeat stabilized or stable to heatSuitable processing methods:Injection moldingInformation provided by Baye.. |
|||
| Melt Flow | 3.8 g/10 min | 3.8 g/10 min | ASTM D1238 |
| LyondellBasell Alathon® M6138 High Density Polyethylene ApplicationsALATHON M 6138, formerly known as XM 6138, is a high density polyethylene resin for use in injection molding applications. This resin exhibits good impact resistance and high stiffness... |
|||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| M. Holland Company PP204 Polypropylene Homopolymer Features: Homopolymer, Low Residuals, Good Stiffness, Low Water CarryoverApprovals: FDA 21 CFR 177.1520Information provided by M. Holland. |
|||
| Melt Flow | 3.8 g/10 min | 3.8 g/10 min | ASTM D1238 |
| I. Stern N2560 General Purpose Crystal Polystyrene Features:Excellent ClarityExcellent Process PropertiesHigh Heat MoldingApplicationsMedical PartsDomestic AppliancesAgency RatingsFDA Title 21 CFR 177.1640UL File E220962Information provided by I. St.. |
|||
| Melt Flow | 3.8 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.8 - 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| LG Chemical SEETEC ST508 Linear Low Density Polyethylene, Cast Film Grade Features: Characteristics- Excellent puncture resistance, tear strength. Excellent sealing and optical properties. Comonomer: Octene-1. Additives- Medium slip agent, Medium antiblocking agentApplica.. |
|||
| Melt Flow | 3.8 g/10 min @Load 21.6 kg, Temperature 230 °C |
3.8 g/10 min @Load 47.6 lb, Temperature 446 °F |
ASTM D1238 |
| Kureha KF Polymer 1550 High Viscosity PVDF Homopolymer KF Polymer is a fire-resistant engineering plastic which maintains the excellent performance of a fluoropolymer. It shows well-balanced molding processability similar to general-purpose resins. KF p.. |
|||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Multibase Multi-Flex® D 5304 Black TPO Thermoplastic Polyolefin Elastomer Forms: PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
| Melt Flow | 3.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® VC-0830 ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 3.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® VC-0830 ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 3.8 g/10 min @Load 10.0 kg, Temperature 250 °C |
3.8 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| SABIC Innovative Plastics NORYL EXT130 PPE+HIPS (Asia Pacific) PPE+PS for auto exterior, High heat |
|||
| Melt Flow | 3.8 g/10 min @Load 5.00 kg, Temperature 190 °C |
3.8 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| SCG Chemicals EL-Leneâ„¢ H570P High Density Polyethylene Pipe Resin Key Characteristics: High stiffness, good processingRecommended Applications: Corrugated pipes, non pressure pipes, conduit, sewage drainage pipesInformation provided by SCG Chemicals |
|||
| Melt Flow | 3.8 g/10 min @Load 5.00 kg, Temperature 140 °C |
3.8 g/10 min @Load 11.0 lb, Temperature 284 °F |
ISO 1133 |
| Borealis Borcell™ HE4873 High Density Polyethylene Borcell™ HE4873 is a fully formulated compound for physical foamed data cable insulation. Borcell™ HE4873 is a high-density polyethylene compound containing blowing agent for the production of foa.. |
|||
| Melt Flow | 3.8 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.8 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Total PSI 960E Polystyrene Polystyrene 960E is a high impact polystyrene designed for extrusion/thermoforming applications that require exceptional resistance to attack from fats and oils. This ESCR material is used for lids .. |
|||
| Melt Flow | 3.8 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.8 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Chi Mei Kibilac® PW-997S ASA Polymer Extrusion |
|||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ExxonMobil LDPE LD 252 Low Density Polyethylene Resin (European Grade) Product Description: LD 525 is a high purity LDPE extrusion coating grade, designed to meet environmental needs for reduced fume emissions during plastics conversion. This grade offers:Low volatiles.. |
|||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 175 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 347 °F |
ASTM D1238 |
| Diamond Polymers Softflex® 6538 Thermoplastic Elastomer Alloy, Clear Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Melt Flow | 3.8 g/10 min @Load 10.0 kg, Temperature 220 °C |
3.8 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Chi Mei Polyrex® PH-888H Polystyrene - High Impact High FDI; high heat |
|||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
| Braskem PB681 LDPE Cast and Blown Film Extrusion, Injection Molding Polyethylene PB681 is a resin produced under high pressure in a tubular reactor. This resin presents excellent 'draw down' (stability to form fine films). The films produced with this resin have excellent optica.. |
|||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Braskem PB681/59 Blown Film Extrusion Low Density Polyethylene Description: PB681/59 is a grade produced under high pressure in a tubular reactor. This resin is used for laminating films mainly on paper substrate. It is also used in the extrusion coating proces.. |
|||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Braskem PB681/59 LDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Lamination film; general purpose. Information provided by Braskem |
|||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Braskem TI60035NB High Impact Copolymer Polypropylene Description: Extra high izod impact, superior low temperature drop impact.Applications: Suggested uses include compounding, automotive, injection molding.Process: Injection Molding. This resin meets.. |
|||
| Melt Flow | 3.8 - 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.8 - 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Iran Petrochemical (PCC) Arak 0640AA LLDPE
(discontinued **) Information provided by Iran Petrochemical Commercial Co. |
|||
| Melt Flow | 3.8 - 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.8 - 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Iran Petrochemical (PCC) Tabriz 0640AA LLDPE
(discontinued **) Information provided by Iran Petrochemical Commercial Co. |
|||
| Melt Flow | 3.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D-1238 |
| Plaskolite Optix® CP - 75 HID General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
| Melt Flow | 3.8 g/10 min @Load 10.0 kg, Temperature 250 °C |
3.8 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| SABIC Innovative Plastics NORYL PX2630 PPE+HIPS (Asia Pacific) PPE+HIPS Unfilled high Impact |
|||
| Melt Flow | 3.8 - 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.8 - 5.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Ineos Nova 610 Crystal Polystyrene GP Grade
(discontinued **) Broad, medium melt flow range, Broad Vicat rangeApplications: Any; Injection Molding and ExtrusionProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise spe.. |
|||